- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 0.05
- 弯曲强度 [MPa]: 135.0
- 热变形温度 [℃]: 175.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 - 1.70 g/cc | 0.0509 - 0.0614 lb/in³ | Average value: 1.54 g/cc Grade Count:22 |
| Water Absorption | 0.0500 - 1.00 % | 0.0500 - 1.00 % | Average value: 0.738 % Grade Count:20 |
| Moisture Absorption at Equilibrium | 0.300 - 0.400 % | 0.300 - 0.400 % | Average value: 0.378 % Grade Count:18 |
| Linear Mold Shrinkage | 0.00100 - 0.00200 cm/cm | 0.00100 - 0.00200 in/in | Average value: 0.00110 cm/cm Grade Count:20 |
| Linear Mold Shrinkage, Transverse | 0.00100 - 0.00500 cm/cm | 0.00100 - 0.00500 in/in | Average value: 0.00400 cm/cm Grade Count:18 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 82.0 - 88.0 | 82.0 - 88.0 | Average value: 85.2 Grade Count:12 |
| Ball Indentation Hardness | 155 - 230 MPa | 22500 - 33400 psi | Average value: 189 MPa Grade Count:16 |
| Tensile Strength, Ultimate | 135 - 210 MPa | 19600 - 30500 psi | Average value: 165 MPa Grade Count:20 |
| Elongation at Break | 2.10 - 6.00 % | 2.10 - 6.00 % | Average value: 3.96 % Grade Count:21 |
| Modulus of Elasticity | 8.96 - 20.0 GPa | 1300 - 2900 ksi | Average value: 15.1 GPa Grade Count:21 |
| Charpy Impact Unnotched | 6.00 - 9.50 J/cm² | 28.6 - 45.2 ft-lb/in² | Average value: 7.93 J/cm² Grade Count:20 |
| 6.00 - 9.50 J/cm² @Temperature -30.0 - 30.0 °C | 28.6 - 45.2 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 7.83 J/cm² Grade Count:20 | |
| Charpy Impact, Notched | 1.20 - 2.50 J/cm² | 5.71 - 11.9 ft-lb/in² | Average value: 1.84 J/cm² Grade Count:20 |
| 1.00 - 2.00 J/cm² @Temperature -30.0 - 30.0 °C | 4.76 - 9.52 ft-lb/in² @Temperature -22.0 - 86.0 °F | Average value: 1.52 J/cm² Grade Count:20 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 1.00e+14 ohm-cm | 1.00e+12 - 1.00e+14 ohm-cm | Average value: 1.13e+13 ohm-cm Grade Count:21 |
| Surface Resistance | 1.00e+11 - 1.00e+12 ohm | 1.00e+11 - 1.00e+12 ohm | Average value: 7.16e+11 ohm Grade Count:19 |
| Dielectric Strength | 17.7 - 55.0 kV/mm | 450 - 1400 kV/in | Average value: 36.2 kV/mm Grade Count:20 |
| Comparative Tracking Index | 60.0 - 600 V | 60.0 - 600 V | Average value: 570 V Grade Count:18 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 10.0 - 37.8 µm/m-°C | 5.56 - 21.0 µin/in-°F | Average value: 16.3 µm/m-°C Grade Count:21 |
| CTE, linear, Transverse to Flow | 70.0 - 120 µm/m-°C | 38.9 - 66.7 µin/in-°F | Average value: 97.2 µm/m-°C Grade Count:18 |
| Melting Point | 178 °C | 352 °F | Average value: 178 °C Grade Count:16 |
| Maximum Service Temperature, Air | 80.0 - 160 °C | 176 - 320 °F | Average value: 126 °C Grade Count:18 |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 - 182 °C | 347 - 360 °F | Average value: 179 °C Grade Count:3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 - 177 °C | 239 - 350 °F | Average value: 162 °C Grade Count:21 |
| Deflection Temperature at 8.0 MPa | 105 - 160 °C | 221 - 320 °F | Average value: 131 °C Grade Count:18 |
| Flammability, UL94 | HB | HB | Grade Count:17 |