- 熔体流动速率 [g/10min]: 50.0
- 密度 [g/cm3]: 1.02
- 缺口冲击强度: 2.2
- 弯曲模量 [MPa]: 1.50
- 热变形温度 [℃]: 177.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.460 g/cc | 0.0166 lb/in³ | ASTM D1895 | ||
| Density | 1.02 g/cc | 0.0368 lb/in³ | Sintered Part; ASTM D792 | ||
| Particle Size | 55 µm | 55 µm | Average D50; Laser Diffraction | ||
| 30 - 100 µm | 30 - 100 µm | Range (D10 to D90); Laser Diffraction | |||
| Melt Flow | 50 g/10 min @Load 5.00 kg, Temperature 235 °C | 50 g/10 min @Load 11.0 lb, Temperature 455 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 48.0 MPa | 6960 psi | XY direction; ASTM D638 | ||
| Elongation at Break | 24 % | 24 % | XY direction; ASTM D638 | ||
| Tensile Modulus | 1.70 GPa | 247 ksi | XY direction; ASTM D638 | ||
| Flexural Modulus | 1.50 GPa | 218 ksi | XY direction; ASTM D790 | ||
| Izod Impact, Notched | 2.20 J/cm | 4.12 ft-lb/in | ASTM D256 | ||
| Izod Impact, Unnotched | 4.40 J/cm | 8.24 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 3.10e+14 ohm-cm | 3.10e+14 ohm-cm | 50% RH; 500V; ASTM D257 | ||
| Surface Resistance | 3.00e+14 ohm | 3.00e+14 ohm | 50% RH; 500V; ASTM D257 | ||
| Dielectric Constant | 2.9 | 2.9 | 50% RH; 500V; ASTM D150 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 181 °C | 358 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 351 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Color | White | ||||