- 熔体流动速率 [g/10min]: 52.5
- 密度 [g/cm3]: 1.01
- 吸水率 [%]: 1.6
- 拉伸强度 [MPa]: 48.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | |
| Water Absorption | 1.6 % | 1.6 % | |
| Melt Flow | 52.5 g/10 min @Load 2.16 kg, Temperature 235 °C | 52.5 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min |
| Tensile Modulus | 1.65 GPa | 239 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 28.7 kV/mm | 729 kV/in | |
| Dissipation Factor | 0.000307 @Frequency 1e+6 Hz | 0.000307 @Frequency 1e+6 Hz | |
| 0.000345 @Frequency 100 Hz | 0.000345 @Frequency 100 Hz | ||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 174 °C | 345 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||