- 密度 [g/cm3]: 1.29
- 吸水率 [%]: 1.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.0 % | 1.0 % | ISO 62 | ||
| Moisture Absorption | 0.500 % | 0.500 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 125 MPa | 18100 psi | conditioned; ISO 2039-1 | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | conditioned; ISO 527-1/-2 | ||
| 130 MPa | 18900 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 4.5 % | 4.5 % | dry; ISO 527-1/-2 | ||
| 4.5 % | 4.5 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 7.10 GPa | 1030 ksi | conditioned; ISO 527-1/-2 | ||
| 7.50 GPa | 1090 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | conditioned; ISO 179/1eU | ||
| 7.50 J/cm² | 35.7 ft-lb/in² | dry; ISO 179/1eU | |||
| 4.50 J/cm² @Temperature 30.0 °C | 21.4 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | dry; ISO 179/1eA | ||
| 1.10 J/cm² | 5.23 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.900 J/cm² @Temperature 30.0 °C | 4.28 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 0.900 J/cm² @Temperature 30.0 °C | 4.28 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 10000 ohm-cm | 10000 ohm-cm | conditioned; IEC 60093 | ||
| Surface Resistance | 1000 ohm | 1000 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 90.0 - 120 °C | 194 - 248 °F | long term; EMS | ||
| 150 °C | 302 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 125 °C | 257 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Automotive | Fuel systems | ||||
| Form | Granules | ||||
| Processing | Injection Molding | ||||
| Product Attributes | Hydrolysis resistant | ||||
| Special Characteristics | Anti-static | ||||
| High impact or impact modified | |||||
| Improved heat resistance | |||||
| Improved UV resistance (outdoor use) | |||||