- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.267
- 拉伸强度 [MPa]: 49.0
- 弯曲模量 [MPa]: 19.4
- 热变形温度 [℃]: 193.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | ASTM D792 | ||
| Water Absorption | 0.10 % @Thickness 3.18 mm, Time 86400 sec | 0.10 % @Thickness 0.125 in, Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 0.90 % | 0.90 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 19.3 GPa | 2800 ksi | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 103 MPa | 14900 psi | ASTM D790 | ||
| Flexural Modulus | 19.4 GPa | 2810 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.267 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 0.500 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 100 - 1000 ohm-cm | 100 - 1000 ohm-cm | ASTM D257 | ||
| Surface Resistance | 10 - 100 ohm | 10 - 100 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 11.0 W/m-K | 76.3 BTU-in/hr-ft²-°F | ASTM C177 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 193 °C @Thickness 6.35 mm | 379 °F @Thickness 0.250 in | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C @Thickness 6.35 mm | 365 °F @Thickness 0.250 in | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 - 277 °C | 500 - 531 °F | |||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| Descriptive Properties | |||||
| Features | Electrically Conductive | ||||
| Thermally Conductive | |||||
| Forms | Pellets | ||||
| Generic Name | Polyamide 12 (Nylon 12) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Uses | Automotive Applications | ||||
| Automotive Under the Hood | |||||
| Consumer Applications | |||||
| Electrical/Electronic Applications | |||||
| Housings | |||||
| Industrial Applications | |||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.
Users of our Advanced Search (registration required) may exclude discontinued materials from search results.