- 吸水率 [%]: 0.25
- 缺口冲击强度: 0.694
- 拉伸强度 [MPa]: 43.4
- 弯曲模量 [MPa]: 3.10
- 热变形温度 [℃]: 168.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Water Absorption | 0.25 % @Thickness 3.17 mm | 0.25 % @Thickness 0.125 in | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 43.4 MPa | 6300 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 - 5.0 % | 4.0 - 5.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 71.0 MPa | 10300 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 1.30 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 10 - 100 ohm-cm | 10 - 100 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 10 - 100 ohm | 10 - 100 ohm | ASTM D257 |
| Shielding Effectiveness | 30 - 60 dB | 30 - 60 dB | 1,000 MHz; PolyOne Internal |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 305 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 238 - 271 °C | 460 - 520 °F | Molding |