- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.16
- 拉伸强度 [MPa]: 39.3
- 弯曲模量 [MPa]: 11.415
- 热变形温度 [℃]: 193.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.68 g/cc | 1.68 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Thickness 3.17 mm | 0.10 % @Thickness 0.125 in | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 39.3 MPa | 5700 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| Elongation at Break | 0.40 % | 0.40 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 14.5 GPa | 2100 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 68.9 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 11.415 GPa | 1655.6 ksi | ASTM D790 |
| Izod Impact, Notched | 0.160 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 0.300 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 10000 - 100000 ohm-cm | 10000 - 100000 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1000 - 30000 ohm | 1000 - 30000 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 20.0 - 24.9 W/m-K | 139 - 173 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 193 °C | 380 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 277 °C | 500 - 530 °F | Molding |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |