- 吸水率 [%]: 0.25
- 缺口冲击强度: 1.82
- 弯曲强度 [MPa]: 117.0
- 弯曲模量 [MPa]: 6.89
- 热变形温度 [℃]: 177.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.234 g/cc | 1.234 g/cc | ASTM D792 |
| Water Absorption | 0.25 % @Thickness 3.17 mm | 0.25 % @Thickness 0.125 in | 24 hr immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0045 cm/cm | 0.0045 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 117 MPa | 17000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 6.89 GPa | 1000 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 152 MPa | 22000 psi | ASTM D790 |
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 1.82 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 3.40 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | Unannealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Unannealed, 0.125 in bars; ASTM D648 |