Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 | ||
Water Absorption | 0.10 % @Thickness 0.508 mm | 0.10 % @Thickness 0.0200 in | 24 hr. Immersion; ASTM D570 | ||
Linear Mold Shrinkage | 0.0079 cm/cm | 0.0079 in/in | ASTM D955 | ||
Mechanical Properties | Metric | English | Comments | ||
Tensile Strength, Ultimate | 43.0 MPa | 6240 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
69.57 MPa | 10090 psi | Type 1 - Rigids, 0.2 in/min, 50% in/in; ASTM D638 | |||
Elongation at Break | 1.6 % | 1.6 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
Tensile Modulus | 0.848 GPa | 123 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
Flexural Strength | 68.40 MPa | 9921 psi | ASTM D790 | ||
Flexural Modulus | 5.52 GPa | 800 ksi | ASTM D790 | ||
Izod Impact, Notched | 0.267 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 0.500 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 | ||
Electrical Properties | Metric | English | Comments | ||
Surface Resistivity per Square | 22000 ohm | 22000 ohm | ASTM D257 | ||
Thermal Properties | Metric | English | Comments | ||
Thermal Conductivity | >= 2.02 W/m-K | >= 14.0 BTU-in/hr-ft²-°F | ASTM C177 | ||
Deflection Temperature at 1.8 MPa (264 psi) | 143.0 °C | 289.4 °F | Unannealed, 0.062 in bars; ASTM D648 | ||
Descriptive Properties | |||||
Product Form | Pellets |
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.