- 熔体流动速率 [g/10min]: 170.0
- 密度 [g/cm3]: 1.02
- 拉伸强度 [MPa]: 30.0
- 热变形温度 [℃]: 100.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.02 g/cc | 0.0368 lb/in³ | |
Moisture Absorption at Equilibrium | <= 0.50 % | <= 0.50 % | Humidity Absorption |
Melt Flow | 170 g/10 min | 170 g/10 min | |
Mechanical Properties | Metric | English | Comments |
Tensile Strength, Yield | 30.0 MPa | 4350 psi | |
Elongation at Break | >= 50 % | >= 50 % | |
Elongation at Yield | 23 % | 23 % | |
Modulus of Elasticity | 0.530 GPa | 76.9 ksi | |
Charpy Impact Unnotched | NB | NB | |
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | |
0.500 J/cm² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | ||
Tensile Creep Modulus, 1 hour | 480 MPa | 69600 psi | |
Tensile Creep Modulus, 1000 hours | 310 MPa | 45000 psi | |
Electrical Properties | Metric | English | Comments |
Electrical Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | |
Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
Dielectric Constant | 3.0 @Frequency 1e+6 Hz | 3.0 @Frequency 1e+6 Hz | |
11 @Frequency 100 Hz | 11 @Frequency 100 Hz | ||
Dielectric Strength | 27.0 kV/mm | 686 kV/in | |
Dissipation Factor | 0.10 @Frequency 1e+6 Hz | 0.10 @Frequency 1e+6 Hz | |
0.16 @Frequency 100 Hz | 0.16 @Frequency 100 Hz | ||
Comparative Tracking Index | 600 V | 600 V | |
Thermal Properties | Metric | English | Comments |
CTE, linear | 100 µm/m-°C @Temperature 20.0 °C | 55.6 µin/in-°F @Temperature 68.0 °F | in flow direction |
CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 20.0 °C | 55.6 µin/in-°F @Temperature 68.0 °F | |
Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | |
Deflection Temperature at 1.8 MPa (264 psi) | 45.0 °C | 113 °F | |
Vicat Softening Point | 130 °C | 266 °F | 50°C/hr/50 N |
Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
HB @Thickness 3.20 mm | HB @Thickness 0.126 in |