- 熔体流动速率 [g/10min]: 60.0
- 密度 [g/cm3]: 1.01
- 吸水率 [%]: 1.0
- 拉伸强度 [MPa]: 48.0
- 热变形温度 [℃]: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | |
| Water Absorption | 1.0 % | 1.0 % | |
| Moisture Absorption at Equilibrium | <= 0.50 % | <= 0.50 % | Humidity Absorption |
| Melt Flow | 60 g/10 min | 60 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 6.0 % | 6.0 % | |
| Modulus of Elasticity | 1.50 GPa | 218 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | |
| 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | ||
| Tensile Creep Modulus, 1 hour | 900 MPa | 131000 psi | |
| Tensile Creep Modulus, 1000 hours | 470 MPa | 68200 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 2.0 @Frequency 1e+6 Hz | 2.0 @Frequency 1e+6 Hz | |
| 3.0 @Frequency 100 Hz | 3.0 @Frequency 100 Hz | ||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | |
| Dissipation Factor | 0.028 @Frequency 1e+6 Hz | 0.028 @Frequency 1e+6 Hz | |
| 0.040 @Frequency 100 Hz | 0.040 @Frequency 100 Hz | ||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 100 µm/m-°C @Temperature 20.0 °C | 55.6 µin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 20.0 °C | 55.6 µin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | |
| Vicat Softening Point | 140 °C | 284 °F | 50°C/hr/50 N |
| UL RTI, Electrical | 110 °C | 230 °F | |
| UL RTI, Mechanical with Impact | 70.0 °C | 158 °F | |
| UL RTI, Mechanical without Impact | 95.0 °C | 203 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||