- 密度 [g/cm3]: 1.03
- 拉伸强度 [MPa]: 27.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.03 g/cc | 0.0372 lb/in³ | |
Mechanical Properties | Metric | English | Comments |
Tensile Strength, Yield | 27.0 MPa | 3920 psi | |
Elongation at Break | >= 50 % | >= 50 % | |
Elongation at Yield | 29 % | 29 % | |
Modulus of Elasticity | 0.420 GPa | 60.9 ksi | |
Charpy Impact Unnotched | NB | NB | |
NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
Charpy Impact, Notched | NB | NB | |
0.700 J/cm² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | ||
Electrical Properties | Metric | English | Comments |
Electrical Resistivity | 2.00e+11 ohm-cm | 2.00e+11 ohm-cm | |
Surface Resistance | 2.00e+13 ohm | 2.00e+13 ohm | |
Dielectric Constant | 4.0 @Frequency 1e+6 Hz | 4.0 @Frequency 1e+6 Hz | |
15 @Frequency 100 Hz | 15 @Frequency 100 Hz | ||
Dielectric Strength | 30.0 kV/mm | 762 kV/in | |
Dissipation Factor | 0.16 @Frequency 100 Hz | 0.16 @Frequency 100 Hz | |
0.19 @Frequency 1e+6 Hz | 0.19 @Frequency 1e+6 Hz | ||
Thermal Properties | Metric | English | Comments |
CTE, linear | <= 50.0 µm/m-°C @Temperature 20.0 °C | <= 27.8 µin/in-°F @Temperature 68.0 °F | |
Vicat Softening Point | 125 °C | 257 °F | 50°C/hr/50 N |