- 密度 [g/cm3]: 1.03
- 拉伸强度 [MPa]: 30.0
- 热变形温度 [℃]: 95.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.50 % @Thickness 1.00 mm, Temperature 23.0 °C | 0.50 % @Thickness 0.0394 in, Temperature 73.4 °F | 50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | 127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2) | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | 127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2) | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ISO 527-1/2 | ||
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-1/2 | ||
| Elongation at Yield | 26 % | 26 % | ISO 527-1/2 | ||
| Tensile Modulus | 0.490 GPa | 71.1 ksi | ISO 527-1/2 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 6.80 J/cm² @Temperature 23.0 °C | 32.4 ft-lb/in² @Temperature 73.4 °F | Partial Break; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.3 @Frequency 1e+6 Hz | 3.3 @Frequency 1e+6 Hz | IEC 60250 | ||
| 10 @Frequency 100 Hz | 10 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | K20/P50; IEC 60243-1 | ||
| Dissipation Factor | 0.10 @Frequency 1e+6 Hz | 0.10 @Frequency 1e+6 Hz | IEC 60250 | ||
| 0.19 @Frequency 100 Hz | 0.19 @Frequency 100 Hz | IEC 60250 | |||
| Comparative Tracking Index | >= 600 V | >= 600 V | Test Solution A, 50 drops; IEC 60112 | ||
| 600 V | 600 V | Test Solution A, 100 drops; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 170 µm/m-°C @Temperature 23.0 - 55.0 °C | 94.4 µin/in-°F @Temperature 73.4 - 131 °F | 45x15x10 mm; ISO 11359 | ||
| Melting Point | 173 °C | 343 °F | Peak Temperature; ISO 3146, ISO 11357 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 °C | 113 °F | ISO 75 | ||
| Vicat Softening Point | 125 °C | 257 °F | 50N; ISO 306 | ||
| 165 °C | 329 °F | 10N; ISO 306 | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||||
| Descriptive Properties | |||||
| Electrolytic Corrosion | A1 Step | IEC 60426 | |||