- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 0.2
- 缺口冲击强度: 2.51
- 拉伸强度 [MPa]: 46.0
- 弯曲模量 [MPa]: 0.380
- 热变形温度 [℃]: 130.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hrs; ASTM D570 |
| Water Absorption at Saturation | 1.1 % | 1.1 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | ASTM D638 |
| Elongation at Break | 260 % | 260 % | ASTM D638 |
| Flexural Modulus | 0.380 GPa | 55.1 ksi | ASTM D790 |
| Izod Impact, Notched | 2.51 J/cm | 4.70 ft-lb/in | ASTM D256 |
| 0.210 J/cm @Temperature -40.0 °C | 0.393 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 184 °C | 363 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |