LATI LATAMID 12 H FE90 Nylon 12 Base Magnetizable Compound

LATI LATAMID 12 H FE90 Nylon 12 Base Magnetizable Compound 物性表: LATI LATAMID 12 H FE90 Nylon 12 Base Magnetizable Compound物性表及特性介绍,LATI LATAMID 12 H FE90 Nylon 12 Base Magnetizable Compound注塑参数详情,如需LATI LATAMID 12 H FE90 Nylon 12 Base Magnetizable Compound下载, 可到相关下载区下载
  • 密度 [g/cm3]: 3.25
  • 缺口冲击强度: 0.32
  • 弯曲强度 [MPa]: 32.0
  • 弯曲模量 [MPa]: 10.5
  • 热变形温度 [℃]: 152.0
 
Physical PropertiesMetricEnglishComments
Density 3.25 g/cc0.117 lb/in³ISO 1183
Linear Mold Shrinkage 0.0050 cm/cm0.0050 in/inLATI
Linear Mold Shrinkage, Transverse 0.0050 cm/cm0.0050 in/inLATI
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 7777ASTM D785
Tensile Strength, Ultimate 32.0 MPa4640 psiISO 527
 15.0 MPa
@Temperature 120 °C
2180 psi
@Temperature 248 °F
ISO 527
 18.0 MPa
@Temperature 90.0 °C
2610 psi
@Temperature 194 °F
ISO 527
 24.0 MPa
@Temperature 60.0 °C
3480 psi
@Temperature 140 °F
ISO 527
Flexural Modulus 10.5 GPa1520 ksiASTM D790
Izod Impact, Notched  0.320 J/cm
@Temperature -40.0 °C
0.599 ft-lb/in
@Temperature -40.0 °F
ASTM D256
 0.320 J/cm
@Temperature -20.0 °C
0.599 ft-lb/in
@Temperature -4.00 °F
ASTM D256
 0.330 J/cm
@Temperature 23.0 °C
0.618 ft-lb/in
@Temperature 73.4 °F
ASTM D256
Charpy Impact Unnotched  0.800 J/cm²
@Temperature -40.0 °C
3.81 ft-lb/in²
@Temperature -40.0 °F
DIN 53453
 0.900 J/cm²
@Temperature 23.0 °C
4.28 ft-lb/in²
@Temperature 73.4 °F
DIN 53453
 0.900 J/cm²
@Temperature -20.0 °C
4.28 ft-lb/in²
@Temperature -4.00 °F
DIN 53453
 
Electrical PropertiesMetricEnglishComments
Surface Resistance 0.265 ohm0.265 ohmIEC 93
Dielectric Strength 0.200 kV/mm
@Thickness 2.00 mm
5.08 kV/in
@Thickness 0.0787 in
IEC 243-1
Comparative Tracking Index 188 V188 VIEC 112
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 152 °C306 °FASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 108 °C226 °FASTM D648
Vicat Softening Point 160 °C320 °F50°C/h 50N; ISO 306
Flammability, UL94 HB
@Thickness 0.710 mm
HB
@Thickness 0.0280 in
 
Processing PropertiesMetricEnglishComments
Melt Temperature 240 - 260 °C464 - 500 °F
Mold Temperature 60.0 - 80.0 °C140 - 176 °F
Drying Temperature 80.0 - 90.0 °C176 - 194 °FKeep the material always warm in a hopper at 70-80°C. Temperature can be reduced when using vacuum ovens.
Dry Time >= 3 hour>= 3 hourDrying time can be reduced when using vacuum ovens.
 
Descriptive Properties
Injection Speedmedium

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47076.html

免责声明: 本文 LATI LATAMID 12 H FE90 Nylon 12 Base Magnetizable Compound 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4