- 密度 [g/cm3]: 1.23
- 缺口冲击强度: 15.0
- 拉伸强度 [MPa]: 120.0
- 弯曲模量 [MPa]: 5.20
- 热变形温度 [℃]: 177.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 120 MPa | 17400 psi | ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527 |
| Tensile Modulus | 6.00 GPa | 870 ksi | ISO 527 |
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
| Flexural Modulus | 5.20 GPa | 754 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 165 - 175 °C | 329 - 347 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 351 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||