- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 1.05
- 拉伸强度 [MPa]: 40.0
- 弯曲模量 [MPa]: 0.350
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.70 % | 0.70 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.05 % | 1.05 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527 |
| Elongation at Break | 400 % | 400 % | ISO 527 |
| Tensile Modulus | 1.10 GPa | 160 ksi | ISO 527 |
| Flexural Strength | 30.0 MPa | 4350 psi | ISO 178 |
| Flexural Modulus | 0.350 GPa | 50.8 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | NB | NB | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 175 °C | 347 °F | ISO 11357 |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |