- 密度 [g/cm3]: 1.24
- 吸水率 [%]: 0.15
- 缺口冲击强度: 1.12
- 弯曲强度 [MPa]: 107.0
- 弯曲模量 [MPa]: 5.20
- 热变形温度 [℃]: 176.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hrs; ASTM D570 |
| Water Absorption at Saturation | 1.0 % | 1.0 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 107 MPa | 15500 psi | ATSM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Modulus | 5.20 GPa | 754 ksi | ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm | 2.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 179 °C | 354 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 176 °C | 349 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ASTM D648 |