- 密度 [g/cm3]: 1.25
- 吸水率 [%]: 1.5
- 缺口冲击强度: 1.0
- 拉伸强度 [MPa]: 90.0
- 弯曲模量 [MPa]: 4.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | DIN 53479 |
| Water Absorption | 1.5 % | 1.5 % | DIN 53495 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ASTM-D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM-D638 |
| Tensile Modulus | 6.00 GPa | 870 ksi | ASTM-D790 |
| Flexural Strength | 140 MPa | 20300 psi | ASTM D790 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.00 J/cm @Temperature 23.0 °C | 1.87 ft-lb/in @Temperature 73.4 °F | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 175 °C | 347 °F | |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |