- 密度 [g/cm3]: 1.01
- 吸水率 [%]: 1.15
- 拉伸强度 [MPa]: 40.0
- 热变形温度 [℃]: 130.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.01 g/cc | 0.0365 lb/in³ | ISO 1183 |
Moisture Absorption at Equilibrium | 0.70 % | 0.70 % | 50% RH; ISO 62 |
Water Absorption at Saturation | 1.15 % | 1.15 % | ISO 62 |
Linear Mold Shrinkage | 0.0080 - 0.0090 cm/cm | 0.0080 - 0.0090 in/in | ISO 2577 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527 |
Elongation at Break | 70 % | 70 % | ISO 527 |
Tensile Modulus | 1.10 GPa | 160 ksi | ISO 527 |
Izod Impact, Unnotched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180 |
Charpy Impact Unnotched | NB | NB | ISO 179 |
Electrical Properties | Metric | English | Comments |
Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 |
Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60250 |
Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
Thermal Properties | Metric | English | Comments |
Melting Point | 175 °C | 347 °F | ISO 11357 |
Maximum Service Temperature, Air | 105 °C | 221 °F | Continuous use |
150 °C | 302 °F | Short peaks operation | |
Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75 |
Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75 |
Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in |