- 密度 [g/cm3]: 1.124
- 缺口冲击强度: 0.35
- 拉伸强度 [MPa]: 49.0
- 弯曲模量 [MPa]: 1.98
- 热变形温度 [℃]: 137.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Density | 1.124 g/cc | 0.04061 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| 0.210 % | 0.210 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec | >= 0.020 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec | 0.020 - 0.040 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | Type I, 5 mm/min; ASTM D638 |
| 44.0 MPa | 6380 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | 5 mm/min; ISO 527 |
| 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 17.1 % | 17.1 % | 5 mm/min; ISO 527 |
| 28.1 % | 28.1 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 11.3 % | 11.3 % | 5 mm/min; ISO 527 |
| 13.4 % | 13.4 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.10 GPa | 305 ksi | 1 mm/min; ISO 527 |
| 2.21 GPa | 321 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 67.0 MPa | 9720 psi | ISO 178 |
| Flexural Modulus | 1.98 GPa | 287 ksi | 2 mm/min; ISO 178 |
| 2.05 GPa | 297 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.350 J/cm | 0.656 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 19.1 J/cm | 35.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 219 kJ/m² | 104 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 2.00 J @Temperature 23.0 °C | 1.48 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.0 - 4.0 ohm | 1.0 - 4.0 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 99.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 55.0 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 108 µm/m-°C @Temperature -30.0 - 30.0 °C | 60.0 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 158 °C @Thickness 3.20 mm | 316 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 96.0 °C @Thickness 3.20 mm | 205 °F @Thickness 0.126 in | unannealed; ASTM D648 | |