- 密度 [g/cm3]: 6.9
- 缺口冲击强度: 0.66
- 拉伸强度 [MPa]: 41.0
- 弯曲模量 [MPa]: 4.46
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 6.90 g/cc | 0.249 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 1.6 % | 1.6 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 5.22 GPa | 757 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 60.0 MPa | 8700 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.46 GPa | 647 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.660 J/cm | 1.24 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.36 J/cm | 6.29 ft-lb/in | ASTM D4812 |