- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 0.14
- 缺口冲击强度: 4.0
- 拉伸强度 [MPa]: 43.0
- 断裂伸长率 [%]: 66.0
- 弯曲模量 [MPa]: 2.30
- 热变形温度 [℃]: 147.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 0.14 % @Time 86400 sec | 0.14 % @Time 24.0 hour | ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm | 0.011 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 6.6 % | 6.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 66.0 MPa | 9570 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.41 | 0.41 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.31 | 0.31 | ASTM D3702 Modified |
| K (wear) Factor | 898 x 10-8 mm³/N-M | 446 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 40.0 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 50.0 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |