TP Composites Elastoblend® PA12 CL

TP Composites Elastoblend® PA12 CL 物性表: TP Composites Elastoblend® PA12 CL物性表及特性介绍,TP Composites Elastoblend® PA12 CL注塑参数详情,如需TP Composites Elastoblend® PA12 CL下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 12.0
  • 密度 [g/cm3]: 1.06
  • 吸水率 [%]: 0.3
  • 缺口冲击强度: 0.534
  • 拉伸强度 [MPa]: 81.4
  • 弯曲模量 [MPa]: 2.03
  • 硬度: 85.0
  • 热变形温度 [℃]: 154.0
  • 透光率 [%]: 90.0
 
Physical PropertiesMetricEnglishComments
Density 1.06 g/cc0.0383 lb/in³ASTM D792
Water Absorption 0.30 %
@Time 86400 sec
0.30 %
@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.011 cm/cm
@Thickness 3.17 mm
0.011 in/in
@Thickness 0.125 in
ASTM D955
Melt Flow 12 g/10 min
@Load 3.80 kg,
Temperature 230 °C
12 g/10 min
@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 8585ASTM D785
Tensile Strength, Yield 81.4 MPa11800 psiASTM D638
Elongation at Yield 10 %10 %ASTM D638
Flexural Strength 98.6 MPa14300 psiASTM D790
Flexural Modulus 2.03 GPa295 ksiASTM D790
Poissons Ratio 0.400.40ASTM E132
Izod Impact, Notched 0.534 J/cm
@Thickness 3.17 mm
1.00 ft-lb/in
@Thickness 0.125 in
ASTM D256
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 72.0 µm/m-°C40.0 µin/in-°FASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 154 °C310 °FUnannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 149 °C300 °FUnannealed; ASTM D648
Vicat Softening Point 108 °C226 °FRate B (120°C/h); ASTM D1525
 
Optical PropertiesMetricEnglishComments
Haze 0.70 %0.70 %ASTM D1003
Transmission, Visible 90.0 %90.0 %transparent; thickness not quantified
IR Transmittance 89 - 90 %89 - 90 %ASTM D1003

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47195.html

免责声明: 本文 TP Composites Elastoblend® PA12 CL 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4