- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 1.9
- 缺口冲击强度: 5.0
- 拉伸强度 [MPa]: 38.0
- 弯曲模量 [MPa]: 1.30
- 热变形温度 [℃]: 131.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO 1183 |
| Water Absorption | 1.9 % @Time 86400 sec | 1.9 % @Time 24.0 hour | ISO 62-1 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 28.0 MPa | 4060 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 2.9 % | 2.9 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.00 GPa | 290 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 45.0 MPa | 6530 psi | break, 2 mm/min; ISO 178 |
| Flexural Modulus | 1.30 GPa | 189 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 85.0 kJ/m² | 40.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 130 µm/m-°C @Temperature 23.0 - 60.0 °C | 72.2 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 140 µm/m-°C @Temperature 23.0 - 60.0 °C | 77.8 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 131 °C | 268 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |