SABIC Innovative Plastics LNP THERMOCOMP SH1100A PA12

SABIC Innovative Plastics LNP THERMOCOMP SH1100A PA12 物性表: SABIC Innovative Plastics LNP THERMOCOMP SH1100A PA12物性表及特性介绍,SABIC Innovative Plastics LNP THERMOCOMP SH1100A PA12注塑参数详情,如需SABIC Innovative Plastics LNP THERMOCOMP SH1100A PA12下载, 可到相关下载区下载
  • 缺口冲击强度: 0.65
  • 断裂伸长率 [%]: 42.0
  • 弯曲模量 [MPa]: 8.70
  • 热变形温度 [℃]: 160.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 11.0 g/cc11.0 g/ccASTM D792
Moisture Absorption 0.0300 %0.0300 %50% RH, 24 hrs; ASTM D570
 0.0500 %0.0500 %23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm
@Time 86400 sec
0.0030 - 0.0050 in/in
@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm
@Time 86400 sec
0.0030 - 0.0050 in/in
@Time 24.0 hour
ASTM D955
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 19.0 MPa2760 psiType I, 5 mm/min; ASTM D638
Elongation at Break 0.50 %0.50 %Type I, 5 mm/min; ASTM D638
 0.50 %0.50 %5 mm/min; ISO 527
Tensile Modulus 4.73 GPa686 ksi1 mm/min; ISO 527
 11.16 GPa1619 ksi5 mm/min; ASTM D638
Flexural Strength 38.0 MPa5510 psibrk, 1.3 mm/min, 50 mm span; ASTM D790
 38.0 MPa5510 psiISO 178
Flexural Yield Strength 42.0 MPa6090 psi1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 8.70 GPa1260 ksi2 mm/min; ISO 178
 10.9 GPa1580 ksi1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.650 J/cm1.22 ft-lb/inASTM D256
Izod Impact, Unnotched 0.880 J/cm1.65 ft-lb/inASTM D4812
Izod Impact, Notched (ISO) 11.0 kJ/m²5.23 ft-lb/in²80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 10.0 kJ/m²4.76 ft-lb/in²80*10*4; ISO 180/1U
Dart Drop, Total Energy 4.00 J
@Temperature 23.0 °C
2.95 ft-lb
@Temperature 73.4 °F
ASTM D3763
Impact Test 1.00 J0.738 ft-lbMultiaxial Impact; ISO 6603
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 31.0 µm/m-°C
@Temperature -30.0 - 30.0 °C
17.2 µin/in-°F
@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 31.0 µm/m-°C
@Temperature -30.0 - 30.0 °C
17.2 µin/in-°F
@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 160 °C320 °FFlatw 80*10*4 sp=64mm; ISO 75/Bf
 161 °C
@Thickness 3.20 mm
322 °F
@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 129 °C264 °FFlatw 80*10*4 sp=64mm; ISO 75/Af
 122 °C
@Thickness 3.20 mm
252 °F
@Thickness 0.126 in
unannealed; ASTM D648

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47188.html

免责声明: 本文 SABIC Innovative Plastics LNP THERMOCOMP SH1100A PA12 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4