Evonik Corporation Trogamid® T5004 Nylon 6-3 Compound

Evonik Corporation Trogamid® T5004 Nylon 6-3 Compound 物性表: Evonik Corporation Trogamid® T5004 Nylon 6-3 Compound物性表及特性介绍,Evonik Corporation Trogamid® T5004 Nylon 6-3 Compound注塑参数详情,如需Evonik Corporation Trogamid® T5004 Nylon 6-3 Compound下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.12
  • 拉伸强度 [MPa]: 90.0
  • 弯曲模量 [MPa]: 3.00
  • 热变形温度 [℃]: 140.0
  • 透光率 [%]: 90.0
 
Physical PropertiesMetricEnglishComments
Density 1.12 g/cc0.0405 lb/in³ISO 1183
Viscosity Test 125 cm³/g125 cm³/gViscosity Number; ISO 307
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore D 8686ISO 868
Ball Indentation Hardness 150 MPa21800 psiH30; ISO 2039-1
Tensile Strength, Yield 90.0 MPa13100 psi50 mm/min; ISO 527-1/2
Elongation at Break >= 50 %>= 50 %50 mm/min; ISO 527-1/2
Elongation at Yield 8.0 %8.0 %50 mm/min; ISO 527-1/2
 8.5 %8.5 %5 mm/min, Outer fiber strain at maximum stress; ISO 178
Tensile Modulus 2.80 GPa406 ksiISO 527-1/2
Flexural Strength 104 MPa15100 psi5 mm/min, at 3.5% Strain; ISO 178
 152 MPa22000 psi5 mm/min; ISO 178
Flexural Modulus 3.00 GPa435 ksiISO 178
Charpy Impact Unnotched  NB
@Temperature 0.000 °C
NB
@Temperature 32.0 °F
ISO 179/1eU
 NB
@Temperature -30.0 °C
NB
@Temperature -22.0 °F
ISO 179/1eU
 NB
@Temperature 23.0 °C
NB
@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched  0.600 J/cm²
@Temperature -30.0 °C
2.86 ft-lb/in²
@Temperature -22.0 °F
ISO 179/1eA
 0.900 J/cm²
@Temperature 0.000 °C
4.28 ft-lb/in²
@Temperature 32.0 °F
ISO 179/1eA
 1.10 J/cm²
@Temperature 23.0 °C
5.24 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1 hour 2500 MPa363000 psiISO 899-1
Tensile Creep Modulus, 1000 hours 1300 MPa189000 psiISO 899-1
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity >= 1.00e+15 ohm-cm>= 1.00e+15 ohm-cmIEC 60093
Surface Resistance >= 1.00e+13 ohm>= 1.00e+13 ohmIEC 60093
 >= 1.00e+15 ohm>= 1.00e+15 ohmSpec.; IEC 60093
Dielectric Constant  3.3
@Frequency 1e+6 Hz
3.3
@Frequency 1e+6 Hz
IEC 60250
 4.2
@Frequency 50 Hz
4.2
@Frequency 50 Hz
IEC 60250
 4.6
@Frequency 100 Hz
4.6
@Frequency 100 Hz
IEC 60250
Dielectric Strength 24.0 kV/mm610 kV/inK20/P50; IEC 60243-1
Dissipation Factor  0.017
@Frequency 50 Hz
0.017
@Frequency 50 Hz
IEC 60250
 0.024
@Frequency 100 Hz
0.024
@Frequency 100 Hz
IEC 60250
 0.028
@Frequency 1e+6 Hz
0.028
@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index >= 600 V>= 600 VTest Solution A, 100 drops; IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear 53.0 µm/m-°C
@Temperature 23.0 - 80.0 °C
29.4 µin/in-°F
@Temperature 73.4 - 176 °F
Longitudinal; ISO 11359
CTE, linear, Transverse to Flow 57.0 µm/m-°C
@Temperature 23.0 - 80.0 °C
31.7 µin/in-°F
@Temperature 73.4 - 176 °F
ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 140 °C284 °FISO 75-1/2
Deflection Temperature at 1.8 MPa (264 psi) 120 °C248 °FISO 75-1/2
Vicat Softening Point 142 °C288 °F50N; ISO 306
 148 °C298 °F10N; ISO 306
Glass Transition Temp, Tg 150 °C302 °FTg, 10 K/min
Flammability, UL94  V-2
@Thickness 0.800 mm
V-2
@Thickness 0.0315 in
 V-2
@Thickness 1.60 mm
V-2
@Thickness 0.0630 in
 
Optical PropertiesMetricEnglishComments
Transmission, Visible 90.0 %90.0 %transparent; thickness not quantified

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47459.html

免责声明: 本文 Evonik Corporation Trogamid® T5004 Nylon 6-3 Compound 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4