- 密度 [g/cm3]: 1.06
- 吸水率 [%]: 1.3
- 成型收缩率 [%]: 0.011
- 缺口冲击强度: 3.0
- 拉伸强度 [MPa]: 54.0
- 弯曲模量 [MPa]: 1.44
- 硬度: 114.0
- 热变形温度 [℃]: 135.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 1.3 % @Temperature 23.0 °C | 1.3 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage | 0.011 cm/cm @Thickness 3.20 mm | 0.011 in/in @Thickness 0.126 in | Flow; DAM | ||
| 0.011 cm/cm @Thickness 3.20 mm | 0.011 in/in @Thickness 0.126 in | Transverse; DAM | |||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm @Thickness 2.00 mm | 0.013 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 114 | 114 | DAM; ISO 2039/2 | ||
| Tensile Strength, Yield | 54.0 MPa @Temperature 23.0 °C | 7830 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 62.0 MPa @Temperature 23.0 °C | 8990 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 17 % @Temperature 23.0 °C | 17 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| Elongation at Yield | 4.5 % @Temperature 23.0 °C | 4.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 18 % @Temperature 23.0 °C | 18 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 1.70 GPa @Temperature 23.0 °C | 247 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 2.40 GPa @Temperature 23.0 °C | 348 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 1.44 GPa @Temperature 23.0 °C | 209 ksi @Temperature 73.4 °F | 50%RH; ISO 178 | ||
| 2.10 GPa @Temperature 23.0 °C | 305 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature -30.0 °C | 1.43 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 180/1A | ||
| 4.00 kJ/m² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 4.50 kJ/m² @Temperature -30.0 °C | 2.14 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | |||
| 4.50 kJ/m² @Temperature 23.0 °C | 2.14 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C | 19.0 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.300 J/cm² @Temperature -30.0 °C | 1.43 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 0.350 J/cm² @Temperature 23.0 °C | 1.67 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 0.350 J/cm² @Temperature -30.0 °C | 1.67 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 0.400 J/cm² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | >= 600 V @Temperature 23.0 °C | >= 600 V @Temperature 73.4 °F | DAM; UL 746A | ||
| >= 600 V @Temperature 23.0 °C | >= 600 V @Temperature 73.4 °F | DAM; ASTM D3638 | |||
| 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | DAM; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 50.0 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | ||
| 120 µm/m-°C @Temperature 23.0 - 55.0 °C | 66.7 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 180 µm/m-°C @Temperature 55.0 - 160 °C | 100 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | DAM; ISO 75-1/-2 | ||
| UL RTI, Electrical | 105 °C @Thickness 0.860 mm | 221 °F @Thickness 0.0339 in | DAM; UL 746B | ||
| 105 °C @Thickness 1.50 mm | 221 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 105 °C @Thickness 3.00 mm | 221 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 0.860 mm | 149 °F @Thickness 0.0339 in | DAM; UL 746B | |||
| 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 65.0 °C @Thickness 0.860 mm | 149 °F @Thickness 0.0339 in | DAM; UL 746B | |||
| Flammability, UL94 | V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | DAM; IEC 60695-11-10 | ||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| V-2 @Thickness 0.860 mm | V-2 @Thickness 0.0339 in | DAM; UL94 | |||
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | DAM; UL94 | |||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | DAM; UL94 | |||
| V-2 @Thickness 0.860 mm | V-2 @Thickness 0.0339 in | DAM; IEC 60695-11-10 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 218 °C | 424 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 250 °C | 482 °F | DAM; Optimum | |||
| 230 - 290 °C | 446 - 554 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.15 % | <= 0.15 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Natural Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 612 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA612< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Unreinforced Resins | DAM | |||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA612 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||