  4. DuPont Performance Polymers Zytel® LC6200 BK385 Nylon 612

DuPont Performance Polymers Zytel® LC6200 BK385 Nylon 612

DuPont Performance Polymers Zytel® LC6200 BK385 Nylon 612 物性表: DuPont Performance Polymers Zytel® LC6200 BK385 Nylon 612物性表及特性介绍,DuPont Performance Polymers Zytel® LC6200 BK385 Nylon 612注塑参数详情,如需DuPont Performance Polymers Zytel® LC6200 BK385 Nylon 612下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.0
  • 缺口冲击强度: 13.0
  • 拉伸强度 [MPa]: 28.0
  • 热变形温度 [℃]: 85.0
 
Physical PropertiesMetricEnglishComments
Density 1.00 g/cc0.0361 lb/in³DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.0276 cm/cm0.0276 in/inParallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0111 cm/cm0.0111 in/inNormal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Stress  0.0200 MPa
@Strain 0.000 %,
Temperature 60.0 °C		2.90 psi
@Strain 0.000 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 0.0300 MPa
@Strain 0.000 %,
Temperature 60.0 °C		4.35 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 0.0500 MPa
@Strain 0.000 %,
Temperature 90.0 °C		7.25 psi
@Strain 0.000 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 0.0500 MPa
@Strain 0.000 %,
Temperature 90.0 °C		7.25 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 0.0700 MPa
@Strain 0.000 %,
Temperature -40.0 °C		10.2 psi
@Strain 0.000 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 0.0700 MPa
@Strain 0.000 %,
Temperature 40.0 °C		10.2 psi
@Strain 0.000 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 0.0800 MPa
@Strain 0.000 %,
Temperature 120 °C		11.6 psi
@Strain 0.000 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 0.0900 MPa
@Strain 0.000 %,
Temperature 120 °C		13.1 psi
@Strain 0.000 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 0.0900 MPa
@Strain 0.000 %,
Temperature 40.0 °C		13.1 psi
@Strain 0.000 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 0.100 MPa
@Strain 0.000 %,
Temperature 150 °C		14.5 psi
@Strain 0.000 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 0.110 MPa
@Strain 0.000 %,
Temperature 150 °C		16.0 psi
@Strain 0.000 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 0.160 MPa
@Strain 0.000 %,
Temperature 23.0 °C		23.2 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 0.180 MPa
@Strain 0.000 %,
Temperature -40.0 °C		26.1 psi
@Strain 0.000 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 0.190 MPa
@Strain 0.000 %,
Temperature 0.000 °C		27.6 psi
@Strain 0.000 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 0.210 MPa
@Strain 0.000 %,
Temperature 0.000 °C		30.5 psi
@Strain 0.000 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 0.250 MPa
@Strain 0.000 %,
Temperature 23.0 °C		36.3 psi
@Strain 0.000 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 0.290 MPa
@Strain 0.000 %,
Temperature -20.0 °C		42.1 psi
@Strain 0.000 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 0.530 MPa
@Strain 0.0300 %,
Temperature -40.0 °C		76.9 psi
@Strain 0.0300 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 0.550 MPa
@Strain 0.0900 %,
Temperature 40.0 °C		79.8 psi
@Strain 0.0900 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 0.750 MPa
@Strain 0.0300 %,
Temperature -40.0 °C		109 psi
@Strain 0.0300 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 0.850 MPa
@Strain 0.110 %,
Temperature 40.0 °C		123 psi
@Strain 0.110 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 0.960 MPa
@Strain 0.0900 %,
Temperature 23.0 °C		139 psi
@Strain 0.0900 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 1.02 MPa
@Strain 0.170 %,
Temperature 40.0 °C		148 psi
@Strain 0.170 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 1.13 MPa
@Strain 0.0800 %,
Temperature 23.0 °C		164 psi
@Strain 0.0800 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 1.21 MPa
@Strain 0.0800 %,
Temperature 0.000 °C		175 psi
@Strain 0.0800 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 1.33 MPa
@Strain 0.0600 %,
Temperature -20.0 °C		193 psi
@Strain 0.0600 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 1.39 MPa
@Strain 0.0700 %,
Temperature -40.0 °C		202 psi
@Strain 0.0700 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 1.39 MPa
@Strain 0.0700 %,
Temperature 0.000 °C		202 psi
@Strain 0.0700 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 1.53 MPa
@Strain 0.200 %,
Temperature 40.0 °C		222 psi
@Strain 0.200 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 1.64 MPa
@Strain 0.0800 %,
Temperature -40.0 °C		238 psi
@Strain 0.0800 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 1.72 MPa
@Strain 0.170 %,
Temperature 23.0 °C		249 psi
@Strain 0.170 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 2.04 MPa
@Strain 0.160 %,
Temperature 23.0 °C		296 psi
@Strain 0.160 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 2.16 MPa
@Strain 0.150 %,
Temperature 0.000 °C		313 psi
@Strain 0.150 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 2.23 MPa
@Strain 0.110 %,
Temperature -40.0 °C		323 psi
@Strain 0.110 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 2.35 MPa
@Strain 0.120 %,
Temperature -20.0 °C		341 psi
@Strain 0.120 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 2.37 MPa
@Strain 0.160 %,
Temperature 0.000 °C		344 psi
@Strain 0.160 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 2.37 MPa
@Strain 0.920 %,
Temperature 90.0 °C		344 psi
@Strain 0.920 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 2.60 MPa
@Strain 0.110 %,
Temperature -40.0 °C		377 psi
@Strain 0.110 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 2.82 MPa
@Strain 3.27 %,
Temperature 150 °C		409 psi
@Strain 3.27 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 2.83 MPa
@Strain 0.440 %,
Temperature 40.0 °C		410 psi
@Strain 0.440 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 2.90 MPa
@Strain 2.19 %,
Temperature 120 °C		421 psi
@Strain 2.19 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 2.92 MPa
@Strain 0.240 %,
Temperature 23.0 °C		424 psi
@Strain 0.240 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 3.02 MPa
@Strain 0.150 %,
Temperature -40.0 °C		438 psi
@Strain 0.150 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 3.08 MPa
@Strain 0.220 %,
Temperature 0.000 °C		447 psi
@Strain 0.220 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 3.18 MPa
@Strain 4.50 %,
Temperature 150 °C		461 psi
@Strain 4.50 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 3.33 MPa
@Strain 0.180 %,
Temperature -20.0 °C		483 psi
@Strain 0.180 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 3.44 MPa
@Strain 0.230 %,
Temperature 0.000 °C		499 psi
@Strain 0.230 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 3.57 MPa
@Strain 0.150 %,
Temperature -40.0 °C		518 psi
@Strain 0.150 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 3.86 MPa
@Strain 0.190 %,
Temperature -40.0 °C		560 psi
@Strain 0.190 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 4.05 MPa
@Strain 0.400 %,
Temperature 23.0 °C		587 psi
@Strain 0.400 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 4.23 MPa
@Strain 0.240 %,
Temperature -20.0 °C		614 psi
@Strain 0.240 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 4.42 MPa
@Strain 0.190 %,
Temperature -40.0 °C		641 psi
@Strain 0.190 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 4.73 MPa
@Strain 0.230 %,
Temperature -40.0 °C		686 psi
@Strain 0.230 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 4.73 MPa
@Strain 4.13 %,
Temperature 120 °C		686 psi
@Strain 4.13 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 5.32 MPa
@Strain 0.230 %,
Temperature -40.0 °C		772 psi
@Strain 0.230 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 5.51 MPa
@Strain 2.96 %,
Temperature 90.0 °C		799 psi
@Strain 2.96 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 5.69 MPa
@Strain 19.51 %,
Temperature 150 °C		825 psi
@Strain 19.51 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 5.95 MPa
@Strain 17.66 %,
Temperature 150 °C		863 psi
@Strain 17.66 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.39 MPa
@Strain 35.26 %,
Temperature 150 °C		927 psi
@Strain 35.26 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 6.69 MPa
@Strain 32.75 %,
Temperature 150 °C		970 psi
@Strain 32.75 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 6.81 MPa
@Strain 51.14 %,
Temperature 150 °C		988 psi
@Strain 51.14 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.10 MPa
@Strain 48.0 %,
Temperature 150 °C		1030 psi
@Strain 48.0 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.14 MPa
@Strain 66.88 %,
Temperature 150 °C		1040 psi
@Strain 66.88 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.34 MPa
@Strain 1.88 %,
Temperature 60.0 °C		1060 psi
@Strain 1.88 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 7.41 MPa
@Strain 63.26 %,
Temperature 150 °C		1070 psi
@Strain 63.26 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.43 MPa
@Strain 82.35 %,
Temperature 150 °C		1080 psi
@Strain 82.35 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.67 MPa
@Strain 78.3 %,
Temperature 150 °C		1110 psi
@Strain 78.3 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.69 MPa
@Strain 97.54 %,
Temperature 150 °C		1120 psi
@Strain 97.54 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 7.75 MPa
@Strain 15.98 %,
Temperature 120 °C		1120 psi
@Strain 15.98 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 7.93 MPa
@Strain 93.16 %,
Temperature 150 °C		1150 psi
@Strain 93.16 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 7.95 MPa
@Strain 112.41 %,
Temperature 150 °C		1150 psi
@Strain 112.41 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.18 MPa
@Strain 107.75 %,
Temperature 150 °C		1190 psi
@Strain 107.75 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.23 MPa
@Strain 126.89 %,
Temperature 150 °C		1190 psi
@Strain 126.89 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.24 MPa
@Strain 17.39 %,
Temperature 120 °C		1200 psi
@Strain 17.39 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 8.42 MPa
@Strain 122.15 %,
Temperature 150 °C		1220 psi
@Strain 122.15 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.52 MPa
@Strain 140.93 %,
Temperature 150 °C		1240 psi
@Strain 140.93 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.69 MPa
@Strain 136.16 %,
Temperature 150 °C		1260 psi
@Strain 136.16 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 8.75 MPa
@Strain 30.85 %,
Temperature 120 °C		1270 psi
@Strain 30.85 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 8.82 MPa
@Strain 154.53 %,
Temperature 150 °C		1280 psi
@Strain 154.53 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 8.97 MPa
@Strain 149.65 %,
Temperature 150 °C		1300 psi
@Strain 149.65 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.12 MPa
@Strain 31.5 %,
Temperature 120 °C		1320 psi
@Strain 31.5 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.13 MPa
@Strain 167.68 %,
Temperature 150 °C		1320 psi
@Strain 167.68 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.27 MPa
@Strain 162.84 %,
Temperature 150 °C		1340 psi
@Strain 162.84 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.28 MPa
@Strain 45.91 %,
Temperature 120 °C		1350 psi
@Strain 45.91 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.44 MPa
@Strain 180.47 %,
Temperature 150 °C		1370 psi
@Strain 180.47 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.57 MPa
@Strain 175.62 %,
Temperature 150 °C		1390 psi
@Strain 175.62 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.62 MPa
@Strain 45.81 %,
Temperature 120 °C		1400 psi
@Strain 45.81 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 9.67 MPa
@Strain 60.87 %,
Temperature 120 °C		1400 psi
@Strain 60.87 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.77 MPa
@Strain 192.86 %,
Temperature 150 °C		1420 psi
@Strain 192.86 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 9.89 MPa
@Strain 188.08 %,
Temperature 150 °C		1430 psi
@Strain 188.08 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 9.98 MPa
@Strain 75.62 %,
Temperature 120 °C		1450 psi
@Strain 75.62 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 9.98 MPa
@Strain 60.03 %,
Temperature 120 °C		1450 psi
@Strain 60.03 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.11 MPa
@Strain 205.16 %,
Temperature 150 °C		1466 psi
@Strain 205.16 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.21 MPa
@Strain 200.29 %,
Temperature 150 °C		1481 psi
@Strain 200.29 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.3 MPa
@Strain 74.13 %,
Temperature 120 °C		1490 psi
@Strain 74.13 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.3 MPa
@Strain 90.08 %,
Temperature 120 °C		1490 psi
@Strain 90.08 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.46 MPa
@Strain 217.24 %,
Temperature 150 °C		1517 psi
@Strain 217.24 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.56 MPa
@Strain 212.4 %,
Temperature 150 °C		1532 psi
@Strain 212.4 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 10.56 MPa
@Strain 87.95 %,
Temperature 120 °C		1532 psi
@Strain 87.95 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.59 MPa
@Strain 104.21 %,
Temperature 120 °C		1536 psi
@Strain 104.21 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.81 MPa
@Strain 229.23 %,
Temperature 150 °C		1568 psi
@Strain 229.23 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 10.84 MPa
@Strain 101.45 %,
Temperature 120 °C		1572 psi
@Strain 101.45 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 10.88 MPa
@Strain 118.11 %,
Temperature 120 °C		1578 psi
@Strain 118.11 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 10.91 MPa
@Strain 224.45 %,
Temperature 150 °C		1582 psi
@Strain 224.45 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.1 MPa
@Strain 114.65 %,
Temperature 120 °C		1610 psi
@Strain 114.65 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.18 MPa
@Strain 241.02 %,
Temperature 150 °C		1622 psi
@Strain 241.02 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.19 MPa
@Strain 131.66 %,
Temperature 120 °C		1623 psi
@Strain 131.66 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.21 MPa
@Strain 4.54 %,
Temperature 60.0 °C		1626 psi
@Strain 4.54 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 11.26 MPa
@Strain 236.28 %,
Temperature 150 °C		1633 psi
@Strain 236.28 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.38 MPa
@Strain 127.51 %,
Temperature 120 °C		1651 psi
@Strain 127.51 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.48 MPa
@Strain 144.92 %,
Temperature 120 °C		1665 psi
@Strain 144.92 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.56 MPa
@Strain 252.8 %,
Temperature 150 °C		1677 psi
@Strain 252.8 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.64 MPa
@Strain 248.09 %,
Temperature 150 °C		1688 psi
@Strain 248.09 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 11.65 MPa
@Strain 140.04 %,
Temperature 120 °C		1690 psi
@Strain 140.04 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 11.7 MPa
@Strain 12.45 %,
Temperature 90.0 °C		1700 psi
@Strain 12.45 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 11.8 MPa
@Strain 157.84 %,
Temperature 120 °C		1710 psi
@Strain 157.84 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 11.8 MPa
@Strain 16.87 %,
Temperature 90.0 °C		1710 psi
@Strain 16.87 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 11.92 MPa
@Strain 264.19 %,
Temperature 150 °C		1729 psi
@Strain 264.19 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 11.94 MPa
@Strain 152.3 %,
Temperature 120 °C		1732 psi
@Strain 152.3 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.0 MPa
@Strain 259.5 %,
Temperature 150 °C		1740 psi
@Strain 259.5 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.14 MPa
@Strain 170.48 %,
Temperature 120 °C		1761 psi
@Strain 170.48 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.23 MPa
@Strain 164.29 %,
Temperature 120 °C		1774 psi
@Strain 164.29 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.28 MPa
@Strain 274.97 %,
Temperature 150 °C		1781 psi
@Strain 274.97 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.4 MPa
@Strain 270.76 %,
Temperature 150 °C		1800 psi
@Strain 270.76 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.47 MPa
@Strain 182.84 %,
Temperature 120 °C		1809 psi
@Strain 182.84 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.55 MPa
@Strain 175.98 %,
Temperature 120 °C		1820 psi
@Strain 175.98 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.64 MPa
@Strain 285.05 %,
Temperature 150 °C		1833 psi
@Strain 285.05 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 12.77 MPa
@Strain 281.4 %,
Temperature 150 °C		1852 psi
@Strain 281.4 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.83 MPa
@Strain 194.84 %,
Temperature 120 °C		1861 psi
@Strain 194.84 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 12.87 MPa
@Strain 187.44 %,
Temperature 120 °C		1867 psi
@Strain 187.44 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 12.9 MPa
@Strain 299.65 %,
Temperature 150 °C		1870 psi
@Strain 299.65 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 12.9 MPa
@Strain 1.80 %,
Temperature 40.0 °C		1870 psi
@Strain 1.80 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 13.04 MPa
@Strain 294.52 %,
Temperature 150 °C		1891 psi
@Strain 294.52 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.09 MPa
@Strain 32.29 %,
Temperature 90.0 °C		1899 psi
@Strain 32.29 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 13.13 MPa
@Strain 296.43 %,
Temperature 150 °C		1904 psi
@Strain 296.43 %,
Temperature 302 °F		50%RH; ISO 11403-1/-2
 13.17 MPa
@Strain 291.54 %,
Temperature 150 °C		1910 psi
@Strain 291.54 %,
Temperature 302 °F		DAM; ISO 11403-1/-2
 13.17 MPa
@Strain 206.68 %,
Temperature 120 °C		1910 psi
@Strain 206.68 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.19 MPa
@Strain 198.59 %,
Temperature 120 °C		1913 psi
@Strain 198.59 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.45 MPa
@Strain 25.47 %,
Temperature 90.0 °C		1951 psi
@Strain 25.47 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 13.53 MPa
@Strain 209.56 %,
Temperature 120 °C		1962 psi
@Strain 209.56 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.56 MPa
@Strain 218.34 %,
Temperature 120 °C		1967 psi
@Strain 218.34 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 13.6 MPa
@Strain 48.45 %,
Temperature 90.0 °C		1970 psi
@Strain 48.45 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 13.71 MPa
@Strain 0.600 %,
Temperature -40.0 °C		1988 psi
@Strain 0.600 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 13.89 MPa
@Strain 64.92 %,
Temperature 90.0 °C		2015 psi
@Strain 64.92 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 13.89 MPa
@Strain 220.36 %,
Temperature 120 °C		2015 psi
@Strain 220.36 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 13.93 MPa
@Strain 229.8 %,
Temperature 120 °C		2020 psi
@Strain 229.8 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.12 MPa
@Strain 39.22 %,
Temperature 90.0 °C		2048 psi
@Strain 39.22 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 14.16 MPa
@Strain 81.48 %,
Temperature 90.0 °C		2054 psi
@Strain 81.48 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 14.26 MPa
@Strain 231.11 %,
Temperature 120 °C		2068 psi
@Strain 231.11 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.33 MPa
@Strain 241.21 %,
Temperature 120 °C		2078 psi
@Strain 241.21 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.43 MPa
@Strain 97.84 %,
Temperature 90.0 °C		2093 psi
@Strain 97.84 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 14.46 MPa
@Strain 53.36 %,
Temperature 90.0 °C		2097 psi
@Strain 53.36 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 14.62 MPa
@Strain 241.81 %,
Temperature 120 °C		2120 psi
@Strain 241.81 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 14.72 MPa
@Strain 113.54 %,
Temperature 90.0 °C		2135 psi
@Strain 113.54 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 14.72 MPa
@Strain 67.68 %,
Temperature 90.0 °C		2135 psi
@Strain 67.68 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 14.74 MPa
@Strain 252.66 %,
Temperature 120 °C		2138 psi
@Strain 252.66 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 14.93 MPa
@Strain 0.710 %,
Temperature -40.0 °C		2165 psi
@Strain 0.710 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 14.95 MPa
@Strain 81.99 %,
Temperature 90.0 °C		2168 psi
@Strain 81.99 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 15.02 MPa
@Strain 252.47 %,
Temperature 120 °C		2178 psi
@Strain 252.47 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.02 MPa
@Strain 128.33 %,
Temperature 90.0 °C		2178 psi
@Strain 128.33 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 15.03 MPa
@Strain 3.85 %,
Temperature 40.0 °C		2180 psi
@Strain 3.85 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 15.15 MPa
@Strain 263.74 %,
Temperature 120 °C		2197 psi
@Strain 263.74 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.19 MPa
@Strain 96.12 %,
Temperature 90.0 °C		2203 psi
@Strain 96.12 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 15.35 MPa
@Strain 142.29 %,
Temperature 90.0 °C		2226 psi
@Strain 142.29 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 15.41 MPa
@Strain 263 %,
Temperature 120 °C		2235 psi
@Strain 263 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.46 MPa
@Strain 109.84 %,
Temperature 90.0 °C		2242 psi
@Strain 109.84 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 15.56 MPa
@Strain 274.47 %,
Temperature 120 °C		2257 psi
@Strain 274.47 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 15.71 MPa
@Strain 122.91 %,
Temperature 90.0 °C		2279 psi
@Strain 122.91 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 15.72 MPa
@Strain 155.6 %,
Temperature 90.0 °C		2280 psi
@Strain 155.6 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 15.82 MPa
@Strain 273.29 %,
Temperature 120 °C		2295 psi
@Strain 273.29 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 15.99 MPa
@Strain 285.08 %,
Temperature 120 °C		2319 psi
@Strain 285.08 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.02 MPa
@Strain 135.38 %,
Temperature 90.0 °C		2324 psi
@Strain 135.38 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 16.11 MPa
@Strain 168.66 %,
Temperature 90.0 °C		2337 psi
@Strain 168.66 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 16.14 MPa
@Strain 283.21 %,
Temperature 120 °C		2341 psi
@Strain 283.21 %,
Temperature 248 °F		DAM; ISO 11403-1/-2
 16.21 MPa
@Strain 294.78 %,
Temperature 120 °C		2351 psi
@Strain 294.78 %,
Temperature 248 °F		50%RH; ISO 11403-1/-2
 16.31 MPa
@Strain 147.19 %,
Temperature 90.0 °C		2366 psi
@Strain 147.19 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 16.52 MPa
@Strain 181.55 %,
Temperature 90.0 °C		2396 psi
@Strain 181.55 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 16.65 MPa
@Strain 158.56 %,
Temperature 90.0 °C		2415 psi
@Strain 158.56 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 16.95 MPa
@Strain 194.43 %,
Temperature 90.0 °C		2458 psi
@Strain 194.43 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 16.99 MPa
@Strain 169.69 %,
Temperature 90.0 °C		2464 psi
@Strain 169.69 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 17.01 MPa
@Strain 19.15 %,
Temperature 60.0 °C		2467 psi
@Strain 19.15 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 17.14 MPa
@Strain 13.0 %,
Temperature 60.0 °C		2486 psi
@Strain 13.0 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 17.36 MPa
@Strain 180.69 %,
Temperature 90.0 °C		2518 psi
@Strain 180.69 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 17.41 MPa
@Strain 207.24 %,
Temperature 90.0 °C		2525 psi
@Strain 207.24 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 17.6 MPa
@Strain 1.36 %,
Temperature 0.000 °C		2550 psi
@Strain 1.36 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 17.77 MPa
@Strain 191.56 %,
Temperature 90.0 °C		2577 psi
@Strain 191.56 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 17.88 MPa
@Strain 219.87 %,
Temperature 90.0 °C		2593 psi
@Strain 219.87 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 18.04 MPa
@Strain 35.26 %,
Temperature 60.0 °C		2616 psi
@Strain 35.26 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.17 MPa
@Strain 202.46 %,
Temperature 90.0 °C		2635 psi
@Strain 202.46 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 18.29 MPa
@Strain 52.4 %,
Temperature 60.0 °C		2653 psi
@Strain 52.4 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.39 MPa
@Strain 232.5 %,
Temperature 90.0 °C		2667 psi
@Strain 232.5 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 18.44 MPa
@Strain 70.13 %,
Temperature 60.0 °C		2675 psi
@Strain 70.13 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.59 MPa
@Strain 213.33 %,
Temperature 90.0 °C		2696 psi
@Strain 213.33 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 18.63 MPa
@Strain 88.02 %,
Temperature 60.0 °C		2702 psi
@Strain 88.02 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.89 MPa
@Strain 105.65 %,
Temperature 60.0 °C		2740 psi
@Strain 105.65 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 18.9 MPa
@Strain 244.94 %,
Temperature 90.0 °C		2740 psi
@Strain 244.94 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 19.01 MPa
@Strain 224.27 %,
Temperature 90.0 °C		2757 psi
@Strain 224.27 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 19.01 MPa
@Strain 7.56 %,
Temperature 40.0 °C		2757 psi
@Strain 7.56 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 19.07 MPa
@Strain 25.19 %,
Temperature 60.0 °C		2766 psi
@Strain 25.19 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 19.19 MPa
@Strain 122.44 %,
Temperature 60.0 °C		2783 psi
@Strain 122.44 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.41 MPa
@Strain 257.22 %,
Temperature 90.0 °C		2815 psi
@Strain 257.22 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 19.44 MPa
@Strain 235.21 %,
Temperature 90.0 °C		2820 psi
@Strain 235.21 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 19.51 MPa
@Strain 137.65 %,
Temperature 60.0 °C		2830 psi
@Strain 137.65 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.75 MPa
@Strain 37.87 %,
Temperature 60.0 °C		2865 psi
@Strain 37.87 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 19.85 MPa
@Strain 150.93 %,
Temperature 60.0 °C		2879 psi
@Strain 150.93 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 19.89 MPa
@Strain 245.98 %,
Temperature 90.0 °C		2885 psi
@Strain 245.98 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 19.94 MPa
@Strain 269.18 %,
Temperature 90.0 °C		2892 psi
@Strain 269.18 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 20.02 MPa
@Strain 50.88 %,
Temperature 60.0 °C		2904 psi
@Strain 50.88 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 20.2 MPa
@Strain 63.96 %,
Temperature 60.0 °C		2930 psi
@Strain 63.96 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 20.25 MPa
@Strain 162.73 %,
Temperature 60.0 °C		2937 psi
@Strain 162.73 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.36 MPa
@Strain 256.65 %,
Temperature 90.0 °C		2953 psi
@Strain 256.65 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 20.4 MPa
@Strain 77.07 %,
Temperature 60.0 °C		2960 psi
@Strain 77.07 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 20.49 MPa
@Strain 280.95 %,
Temperature 90.0 °C		2972 psi
@Strain 280.95 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 20.63 MPa
@Strain 90.3 %,
Temperature 60.0 °C		2992 psi
@Strain 90.3 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 20.72 MPa
@Strain 174.03 %,
Temperature 60.0 °C		3005 psi
@Strain 174.03 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 20.82 MPa
@Strain 267.18 %,
Temperature 90.0 °C		3020 psi
@Strain 267.18 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 20.87 MPa
@Strain 11.52 %,
Temperature 40.0 °C		3027 psi
@Strain 11.52 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 20.89 MPa
@Strain 103.68 %,
Temperature 60.0 °C		3030 psi
@Strain 103.68 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 20.92 MPa
@Strain 313.56 %,
Temperature 90.0 °C		3034 psi
@Strain 313.56 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 20.97 MPa
@Strain 2.95 %,
Temperature 23.0 °C		3041 psi
@Strain 2.95 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 21.0 MPa
@Strain 5.34 %,
Temperature 40.0 °C		3050 psi
@Strain 5.34 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 21.04 MPa
@Strain 292.45 %,
Temperature 90.0 °C		3052 psi
@Strain 292.45 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 21.06 MPa
@Strain 277.32 %,
Temperature 90.0 °C		3055 psi
@Strain 277.32 %,
Temperature 194 °F		DAM; ISO 11403-1/-2
 21.15 MPa
@Strain 117.28 %,
Temperature 60.0 °C		3068 psi
@Strain 117.28 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 21.22 MPa
@Strain 185.65 %,
Temperature 60.0 °C		3078 psi
@Strain 185.65 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.45 MPa
@Strain 130.83 %,
Temperature 60.0 °C		3111 psi
@Strain 130.83 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 21.54 MPa
@Strain 2.11 %,
Temperature 23.0 °C		3124 psi
@Strain 2.11 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 21.63 MPa
@Strain 303.65 %,
Temperature 90.0 °C		3137 psi
@Strain 303.65 %,
Temperature 194 °F		50%RH; ISO 11403-1/-2
 21.72 MPa
@Strain 198.05 %,
Temperature 60.0 °C		3150 psi
@Strain 198.05 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 21.74 MPa
@Strain 144.06 %,
Temperature 60.0 °C		3153 psi
@Strain 144.06 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 21.83 MPa
@Strain 15.69 %,
Temperature 40.0 °C		3166 psi
@Strain 15.69 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.0 MPa
@Strain 156.52 %,
Temperature 60.0 °C		3190 psi
@Strain 156.52 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 22.23 MPa
@Strain 211.25 %,
Temperature 60.0 °C		3224 psi
@Strain 211.25 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.32 MPa
@Strain 167.93 %,
Temperature 60.0 °C		3237 psi
@Strain 167.93 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 22.37 MPa
@Strain 20.02 %,
Temperature 40.0 °C		3245 psi
@Strain 20.02 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.55 MPa
@Strain 68.63 %,
Temperature 40.0 °C		3271 psi
@Strain 68.63 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.55 MPa
@Strain 73.8 %,
Temperature 40.0 °C		3271 psi
@Strain 73.8 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.58 MPa
@Strain 78.98 %,
Temperature 40.0 °C		3275 psi
@Strain 78.98 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.59 MPa
@Strain 63.51 %,
Temperature 40.0 °C		3276 psi
@Strain 63.51 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.6 MPa
@Strain 84.17 %,
Temperature 40.0 °C		3280 psi
@Strain 84.17 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.63 MPa
@Strain 58.4 %,
Temperature 40.0 °C		3282 psi
@Strain 58.4 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.64 MPa
@Strain 89.43 %,
Temperature 40.0 °C		3284 psi
@Strain 89.43 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.66 MPa
@Strain 24.42 %,
Temperature 40.0 °C		3287 psi
@Strain 24.42 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.68 MPa
@Strain 53.34 %,
Temperature 40.0 °C		3289 psi
@Strain 53.34 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.7 MPa
@Strain 178.24 %,
Temperature 60.0 °C		3290 psi
@Strain 178.24 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 22.71 MPa
@Strain 94.73 %,
Temperature 40.0 °C		3294 psi
@Strain 94.73 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.74 MPa
@Strain 48.33 %,
Temperature 40.0 °C		3298 psi
@Strain 48.33 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.77 MPa
@Strain 224.9 %,
Temperature 60.0 °C		3303 psi
@Strain 224.9 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 22.8 MPa
@Strain 43.37 %,
Temperature 40.0 °C		3310 psi
@Strain 43.37 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.8 MPa
@Strain 100.04 %,
Temperature 40.0 °C		3310 psi
@Strain 100.04 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.81 MPa
@Strain 29.03 %,
Temperature 40.0 °C		3308 psi
@Strain 29.03 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.85 MPa
@Strain 33.72 %,
Temperature 40.0 °C		3314 psi
@Strain 33.72 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 22.85 MPa
@Strain 38.5 %,
Temperature 40.0 °C		3314 psi
@Strain 38.5 %,
Temperature 104 °F		50%RH; ISO 11403-1/-2
 23.1 MPa
@Strain 187.84 %,
Temperature 60.0 °C		3350 psi
@Strain 187.84 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 23.16 MPa
@Strain 9.35 %,
Temperature 40.0 °C		3359 psi
@Strain 9.35 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 23.34 MPa
@Strain 238.58 %,
Temperature 60.0 °C		3385 psi
@Strain 238.58 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 23.51 MPa
@Strain 197.35 %,
Temperature 60.0 °C		3410 psi
@Strain 197.35 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 23.93 MPa
@Strain 207.11 %,
Temperature 60.0 °C		3471 psi
@Strain 207.11 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 23.93 MPa
@Strain 251.94 %,
Temperature 60.0 °C		3471 psi
@Strain 251.94 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 24.23 MPa
@Strain 13.55 %,
Temperature 40.0 °C		3514 psi
@Strain 13.55 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 24.34 MPa
@Strain 217.27 %,
Temperature 60.0 °C		3530 psi
@Strain 217.27 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 24.54 MPa
@Strain 264.68 %,
Temperature 60.0 °C		3559 psi
@Strain 264.68 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 24.76 MPa
@Strain 227.91 %,
Temperature 60.0 °C		3591 psi
@Strain 227.91 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 24.84 MPa
@Strain 17.81 %,
Temperature 40.0 °C		3603 psi
@Strain 17.81 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 24.85 MPa
@Strain 2.10 %,
Temperature 0.000 °C		3604 psi
@Strain 2.10 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 25.05 MPa
@Strain 75.46 %,
Temperature 40.0 °C		3633 psi
@Strain 75.46 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.07 MPa
@Strain 70.38 %,
Temperature 40.0 °C		3636 psi
@Strain 70.38 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.08 MPa
@Strain 80.52 %,
Temperature 40.0 °C		3638 psi
@Strain 80.52 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.09 MPa
@Strain 65.32 %,
Temperature 40.0 °C		3639 psi
@Strain 65.32 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.14 MPa
@Strain 85.69 %,
Temperature 40.0 °C		3646 psi
@Strain 85.69 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.14 MPa
@Strain 60.33 %,
Temperature 40.0 °C		3646 psi
@Strain 60.33 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.18 MPa
@Strain 276.85 %,
Temperature 60.0 °C		3652 psi
@Strain 276.85 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.19 MPa
@Strain 22.16 %,
Temperature 40.0 °C		3654 psi
@Strain 22.16 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.2 MPa
@Strain 90.87 %,
Temperature 40.0 °C		3650 psi
@Strain 90.87 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.2 MPa
@Strain 55.37 %,
Temperature 40.0 °C		3650 psi
@Strain 55.37 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.22 MPa
@Strain 238.91 %,
Temperature 60.0 °C		3658 psi
@Strain 238.91 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 25.27 MPa
@Strain 96.05 %,
Temperature 40.0 °C		3665 psi
@Strain 96.05 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.28 MPa
@Strain 50.42 %,
Temperature 40.0 °C		3667 psi
@Strain 50.42 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.31 MPa
@Strain 100.77 %,
Temperature 40.0 °C		3671 psi
@Strain 100.77 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.35 MPa
@Strain 45.53 %,
Temperature 40.0 °C		3677 psi
@Strain 45.53 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.38 MPa
@Strain 26.66 %,
Temperature 40.0 °C		3681 psi
@Strain 26.66 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.41 MPa
@Strain 40.72 %,
Temperature 40.0 °C		3685 psi
@Strain 40.72 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.45 MPa
@Strain 31.26 %,
Temperature 40.0 °C		3691 psi
@Strain 31.26 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.45 MPa
@Strain 35.92 %,
Temperature 40.0 °C		3691 psi
@Strain 35.92 %,
Temperature 104 °F		DAM; ISO 11403-1/-2
 25.69 MPa
@Strain 250.13 %,
Temperature 60.0 °C		3726 psi
@Strain 250.13 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 25.82 MPa
@Strain 288.57 %,
Temperature 60.0 °C		3745 psi
@Strain 288.57 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 25.94 MPa
@Strain 322.13 %,
Temperature 60.0 °C		3762 psi
@Strain 322.13 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 26.08 MPa
@Strain 271.73 %,
Temperature 60.0 °C		3783 psi
@Strain 271.73 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 26.08 MPa
@Strain 6.11 %,
Temperature 23.0 °C		3783 psi
@Strain 6.11 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.16 MPa
@Strain 261.32 %,
Temperature 60.0 °C		3794 psi
@Strain 261.32 %,
Temperature 140 °F		DAM; ISO 11403-1/-2
 26.46 MPa
@Strain 65.41 %,
Temperature 23.0 °C		3838 psi
@Strain 65.41 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.47 MPa
@Strain 71.19 %,
Temperature 23.0 °C		3839 psi
@Strain 71.19 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.5 MPa
@Strain 300.06 %,
Temperature 60.0 °C		3840 psi
@Strain 300.06 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 26.55 MPa
@Strain 76.97 %,
Temperature 23.0 °C		3851 psi
@Strain 76.97 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.64 MPa
@Strain 82.74 %,
Temperature 23.0 °C		3864 psi
@Strain 82.74 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.69 MPa
@Strain 88.47 %,
Temperature 23.0 °C		3871 psi
@Strain 88.47 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.72 MPa
@Strain 59.61 %,
Temperature 23.0 °C		3875 psi
@Strain 59.61 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.74 MPa
@Strain 94.29 %,
Temperature 23.0 °C		3878 psi
@Strain 94.29 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 26.78 MPa
@Strain 100.05 %,
Temperature 23.0 °C		3884 psi
@Strain 100.05 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.19 MPa
@Strain 53.86 %,
Temperature 23.0 °C		3944 psi
@Strain 53.86 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.2 MPa
@Strain 311.55 %,
Temperature 60.0 °C		3950 psi
@Strain 311.55 %,
Temperature 140 °F		50%RH; ISO 11403-1/-2
 27.71 MPa
@Strain 48.32 %,
Temperature 23.0 °C		4019 psi
@Strain 48.32 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 27.84 MPa
@Strain 9.53 %,
Temperature 23.0 °C		4038 psi
@Strain 9.53 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.18 MPa
@Strain 43.08 %,
Temperature 23.0 °C		4087 psi
@Strain 43.08 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.55 MPa
@Strain 71.24 %,
Temperature 23.0 °C		4141 psi
@Strain 71.24 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 28.57 MPa
@Strain 38.1 %,
Temperature 23.0 °C		4144 psi
@Strain 38.1 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.66 MPa
@Strain 77.01 %,
Temperature 23.0 °C		4157 psi
@Strain 77.01 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 28.68 MPa
@Strain 65.48 %,
Temperature 23.0 °C		4160 psi
@Strain 65.48 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 28.69 MPa
@Strain 13.13 %,
Temperature 23.0 °C		4161 psi
@Strain 13.13 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 28.72 MPa
@Strain 82.75 %,
Temperature 23.0 °C		4165 psi
@Strain 82.75 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 28.79 MPa
@Strain 88.51 %,
Temperature 23.0 °C		4176 psi
@Strain 88.51 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 28.81 MPa
@Strain 100.06 %,
Temperature 23.0 °C		4179 psi
@Strain 100.06 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 28.83 MPa
@Strain 94.28 %,
Temperature 23.0 °C		4181 psi
@Strain 94.28 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 28.88 MPa
@Strain 33.39 %,
Temperature 23.0 °C		4189 psi
@Strain 33.39 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.1 MPa
@Strain 16.85 %,
Temperature 23.0 °C		4220 psi
@Strain 16.85 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.1 MPa
@Strain 59.73 %,
Temperature 23.0 °C		4220 psi
@Strain 59.73 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 29.11 MPa
@Strain 28.96 %,
Temperature 23.0 °C		4222 psi
@Strain 28.96 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.24 MPa
@Strain 24.76 %,
Temperature 23.0 °C		4241 psi
@Strain 24.76 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.26 MPa
@Strain 20.72 %,
Temperature 23.0 °C		4244 psi
@Strain 20.72 %,
Temperature 73.4 °F		50%RH; ISO 11403-1/-2
 29.26 MPa
@Strain 2.11 %,
Temperature -20.0 °C		4244 psi
@Strain 2.11 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 29.68 MPa
@Strain 54.05 %,
Temperature 23.0 °C		4305 psi
@Strain 54.05 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 30.2 MPa
@Strain 48.58 %,
Temperature 23.0 °C		4380 psi
@Strain 48.58 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 30.66 MPa
@Strain 43.39 %,
Temperature 23.0 °C		4447 psi
@Strain 43.39 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 30.85 MPa
@Strain 5.02 %,
Temperature 23.0 °C		4474 psi
@Strain 5.02 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 31.04 MPa
@Strain 38.4 %,
Temperature 23.0 °C		4502 psi
@Strain 38.4 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 31.39 MPa
@Strain 33.63 %,
Temperature 23.0 °C		4553 psi
@Strain 33.63 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 31.69 MPa
@Strain 29.06 %,
Temperature 23.0 °C		4596 psi
@Strain 29.06 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 31.95 MPa
@Strain 24.68 %,
Temperature 23.0 °C		4634 psi
@Strain 24.68 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 32.09 MPa
@Strain 8.58 %,
Temperature 23.0 °C		4654 psi
@Strain 8.58 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 32.15 MPa
@Strain 20.45 %,
Temperature 23.0 °C		4663 psi
@Strain 20.45 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 32.28 MPa
@Strain 16.35 %,
Temperature 23.0 °C		4682 psi
@Strain 16.35 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 32.3 MPa
@Strain 12.4 %,
Temperature 23.0 °C		4680 psi
@Strain 12.4 %,
Temperature 73.4 °F		DAM; ISO 11403-1/-2
 33.18 MPa
@Strain 60.93 %,
Temperature 0.000 °C		4812 psi
@Strain 60.93 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 33.49 MPa
@Strain 94.46 %,
Temperature 0.000 °C		4857 psi
@Strain 94.46 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 33.55 MPa
@Strain 66.5 %,
Temperature 0.000 °C		4866 psi
@Strain 66.5 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 33.59 MPa
@Strain 100.05 %,
Temperature 0.000 °C		4872 psi
@Strain 100.05 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 33.59 MPa
@Strain 1.94 %,
Temperature -40.0 °C		4872 psi
@Strain 1.94 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 33.63 MPa
@Strain 88.85 %,
Temperature 0.000 °C		4878 psi
@Strain 88.85 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 33.7 MPa
@Strain 77.65 %,
Temperature 0.000 °C		4890 psi
@Strain 77.65 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 33.76 MPa
@Strain 72.07 %,
Temperature 0.000 °C		4896 psi
@Strain 72.07 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 33.83 MPa
@Strain 83.24 %,
Temperature 0.000 °C		4907 psi
@Strain 83.24 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 34.17 MPa
@Strain 66.8 %,
Temperature 0.000 °C		4956 psi
@Strain 66.8 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 34.23 MPa
@Strain 55.21 %,
Temperature 0.000 °C		4965 psi
@Strain 55.21 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 34.56 MPa
@Strain 1.80 %,
Temperature -40.0 °C		5013 psi
@Strain 1.80 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 34.57 MPa
@Strain 61.24 %,
Temperature 0.000 °C		5014 psi
@Strain 61.24 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 34.58 MPa
@Strain 88.95 %,
Temperature 0.000 °C		5015 psi
@Strain 88.95 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 34.66 MPa
@Strain 100.06 %,
Temperature 0.000 °C		5027 psi
@Strain 100.06 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 34.69 MPa
@Strain 83.39 %,
Temperature 0.000 °C		5031 psi
@Strain 83.39 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 34.74 MPa
@Strain 72.3 %,
Temperature 0.000 °C		5039 psi
@Strain 72.3 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 34.79 MPa
@Strain 94.5 %,
Temperature 0.000 °C		5046 psi
@Strain 94.5 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 34.84 MPa
@Strain 77.86 %,
Temperature 0.000 °C		5053 psi
@Strain 77.86 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 35.63 MPa
@Strain 55.55 %,
Temperature 0.000 °C		5168 psi
@Strain 55.55 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 35.74 MPa
@Strain 3.89 %,
Temperature 0.000 °C		5184 psi
@Strain 3.89 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 35.78 MPa
@Strain 49.48 %,
Temperature 0.000 °C		5189 psi
@Strain 49.48 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 36.48 MPa
@Strain 49.95 %,
Temperature 0.000 °C		5291 psi
@Strain 49.95 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 36.64 MPa
@Strain 4.94 %,
Temperature 0.000 °C		5314 psi
@Strain 4.94 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 36.84 MPa
@Strain 54.18 %,
Temperature -20.0 °C		5343 psi
@Strain 54.18 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 36.9 MPa
@Strain 43.91 %,
Temperature 0.000 °C		5350 psi
@Strain 43.91 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 37.15 MPa
@Strain 59.9 %,
Temperature -20.0 °C		5388 psi
@Strain 59.9 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 37.25 MPa
@Strain 88.62 %,
Temperature -20.0 °C		5403 psi
@Strain 88.62 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 37.34 MPa
@Strain 82.86 %,
Temperature -20.0 °C		5416 psi
@Strain 82.86 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 37.36 MPa
@Strain 71.38 %,
Temperature -20.0 °C		5419 psi
@Strain 71.38 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 37.4 MPa
@Strain 77.13 %,
Temperature -20.0 °C		5420 psi
@Strain 77.13 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 37.41 MPa
@Strain 44.46 %,
Temperature 0.000 °C		5426 psi
@Strain 44.46 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 37.46 MPa
@Strain 65.63 %,
Temperature -20.0 °C		5433 psi
@Strain 65.63 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 37.5 MPa
@Strain 94.32 %,
Temperature -20.0 °C		5440 psi
@Strain 94.32 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 37.65 MPa
@Strain 100.06 %,
Temperature -20.0 °C		5461 psi
@Strain 100.06 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 37.83 MPa
@Strain 38.59 %,
Temperature 0.000 °C		5487 psi
@Strain 38.59 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 38.11 MPa
@Strain 39.07 %,
Temperature 0.000 °C		5527 psi
@Strain 39.07 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 38.44 MPa
@Strain 33.5 %,
Temperature 0.000 °C		5575 psi
@Strain 33.5 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 38.64 MPa
@Strain 48.2 %,
Temperature -20.0 °C		5604 psi
@Strain 48.2 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 38.67 MPa
@Strain 33.82 %,
Temperature 0.000 °C		5609 psi
@Strain 33.82 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 38.93 MPa
@Strain 28.64 %,
Temperature 0.000 °C		5646 psi
@Strain 28.64 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 39.26 MPa
@Strain 8.21 %,
Temperature 0.000 °C		5694 psi
@Strain 8.21 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 39.29 MPa
@Strain 28.79 %,
Temperature 0.000 °C		5699 psi
@Strain 28.79 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 39.42 MPa
@Strain 24.07 %,
Temperature 0.000 °C		5717 psi
@Strain 24.07 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 39.69 MPa
@Strain 19.78 %,
Temperature 0.000 °C		5757 psi
@Strain 19.78 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 39.75 MPa
@Strain 23.94 %,
Temperature 0.000 °C		5765 psi
@Strain 23.94 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 39.89 MPa
@Strain 15.68 %,
Temperature 0.000 °C		5786 psi
@Strain 15.68 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 39.92 MPa
@Strain 11.82 %,
Temperature 0.000 °C		5790 psi
@Strain 11.82 %,
Temperature 32.0 °F		50%RH; ISO 11403-1/-2
 40.18 MPa
@Strain 19.32 %,
Temperature 0.000 °C		5828 psi
@Strain 19.32 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 40.35 MPa
@Strain 7.09 %,
Temperature 0.000 °C		5852 psi
@Strain 7.09 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 40.63 MPa
@Strain 14.93 %,
Temperature 0.000 °C		5893 psi
@Strain 14.93 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 40.8 MPa
@Strain 10.85 %,
Temperature 0.000 °C		5920 psi
@Strain 10.85 %,
Temperature 32.0 °F		DAM; ISO 11403-1/-2
 42.54 MPa
@Strain 42.05 %,
Temperature -20.0 °C		6170 psi
@Strain 42.05 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 43.13 MPa
@Strain 29.54 %,
Temperature -40.0 °C		6255 psi
@Strain 29.54 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 43.54 MPa
@Strain 26.81 %,
Temperature -40.0 °C		6315 psi
@Strain 26.81 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 43.62 MPa
@Strain 24.92 %,
Temperature -40.0 °C		6327 psi
@Strain 24.92 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 44.03 MPa
@Strain 22.36 %,
Temperature -40.0 °C		6386 psi
@Strain 22.36 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 44.15 MPa
@Strain 23.08 %,
Temperature -40.0 °C		6403 psi
@Strain 23.08 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 44.17 MPa
@Strain 4.87 %,
Temperature -20.0 °C		6406 psi
@Strain 4.87 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 44.19 MPa
@Strain 21.86 %,
Temperature -40.0 °C		6409 psi
@Strain 21.86 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 44.39 MPa
@Strain 19.86 %,
Temperature -40.0 °C		6438 psi
@Strain 19.86 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 44.48 MPa
@Strain 20.94 %,
Temperature -40.0 °C		6451 psi
@Strain 20.94 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 44.8 MPa
@Strain 36.24 %,
Temperature -20.0 °C		6500 psi
@Strain 36.24 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 45.51 MPa
@Strain 3.22 %,
Temperature -40.0 °C		6601 psi
@Strain 3.22 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 45.73 MPa
@Strain 18.98 %,
Temperature -40.0 °C		6633 psi
@Strain 18.98 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 46.18 MPa
@Strain 30.75 %,
Temperature -20.0 °C		6698 psi
@Strain 30.75 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 47.02 MPa
@Strain 25.61 %,
Temperature -20.0 °C		6820 psi
@Strain 25.61 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 47.34 MPa
@Strain 3.08 %,
Temperature -40.0 °C		6866 psi
@Strain 3.08 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 47.75 MPa
@Strain 20.77 %,
Temperature -20.0 °C		6926 psi
@Strain 20.77 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 47.91 MPa
@Strain 8.21 %,
Temperature -20.0 °C		6949 psi
@Strain 8.21 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 48.26 MPa
@Strain 16.26 %,
Temperature -20.0 °C		7000 psi
@Strain 16.26 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 48.44 MPa
@Strain 12.06 %,
Temperature -20.0 °C		7026 psi
@Strain 12.06 %,
Temperature -4.00 °F		50%RH; ISO 11403-1/-2
 53.18 MPa
@Strain 4.52 %,
Temperature -40.0 °C		7713 psi
@Strain 4.52 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 55.25 MPa
@Strain 4.42 %,
Temperature -40.0 °C		8013 psi
@Strain 4.42 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 56.4 MPa
@Strain 20.9 %,
Temperature -40.0 °C		8180 psi
@Strain 20.9 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 57.49 MPa
@Strain 18.03 %,
Temperature -40.0 °C		8338 psi
@Strain 18.03 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 57.69 MPa
@Strain 5.84 %,
Temperature -40.0 °C		8367 psi
@Strain 5.84 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 59.59 MPa
@Strain 16.58 %,
Temperature -40.0 °C		8643 psi
@Strain 16.58 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 59.85 MPa
@Strain 19.29 %,
Temperature -40.0 °C		8681 psi
@Strain 19.29 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 59.85 MPa
@Strain 5.83 %,
Temperature -40.0 °C		8681 psi
@Strain 5.83 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 59.95 MPa
@Strain 7.35 %,
Temperature -40.0 °C		8695 psi
@Strain 7.35 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 60.19 MPa
@Strain 15.13 %,
Temperature -40.0 °C		8730 psi
@Strain 15.13 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 60.57 MPa
@Strain 13.6 %,
Temperature -40.0 °C		8785 psi
@Strain 13.6 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 60.95 MPa
@Strain 8.91 %,
Temperature -40.0 °C		8840 psi
@Strain 8.91 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 60.99 MPa
@Strain 12.04 %,
Temperature -40.0 °C		8846 psi
@Strain 12.04 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 61.22 MPa
@Strain 10.5 %,
Temperature -40.0 °C		8879 psi
@Strain 10.5 %,
Temperature -40.0 °F		DAM; ISO 11403-1/-2
 61.24 MPa
@Strain 17.61 %,
Temperature -40.0 °C		8882 psi
@Strain 17.61 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 62.07 MPa
@Strain 15.93 %,
Temperature -40.0 °C		9003 psi
@Strain 15.93 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 62.14 MPa
@Strain 7.35 %,
Temperature -40.0 °C		9013 psi
@Strain 7.35 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 62.61 MPa
@Strain 14.17 %,
Temperature -40.0 °C		9081 psi
@Strain 14.17 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 62.95 MPa
@Strain 12.44 %,
Temperature -40.0 °C		9130 psi
@Strain 12.44 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 63.0 MPa
@Strain 9.00 %,
Temperature -40.0 °C		9140 psi
@Strain 9.00 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
 63.13 MPa
@Strain 10.68 %,
Temperature -40.0 °C		9156 psi
@Strain 10.68 %,
Temperature -40.0 °F		50%RH; ISO 11403-1/-2
Tensile Strength, Yield  28.0 MPa
@Temperature 23.0 °C		4060 psi
@Temperature 73.4 °F		50%RH; ISO 527
 30.0 MPa
@Temperature 23.0 °C		4350 psi
@Temperature 73.4 °F		DAM; ISO 527
Elongation at Break  230 %
@Temperature 23.0 °C		230 %
@Temperature 73.4 °F		DAM; nominal; ISO 527
 250 %
@Temperature 23.0 °C		250 %
@Temperature 73.4 °F		50%RH; nominal; ISO 527
 290 %
@Temperature 23.0 °C		290 %
@Temperature 73.4 °F		50mm/min; 50%RH; ISO 527
 300 %
@Temperature 23.0 °C		300 %
@Temperature 73.4 °F		50mm/min; DAM; ISO 527
Elongation at Yield  20 %
@Temperature 23.0 °C		20 %
@Temperature 73.4 °F		DAM; ISO 527
 30 %
@Temperature 23.0 °C		30 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  0.720 GPa
@Temperature 23.0 °C		104 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 1.08 GPa
@Temperature 23.0 °C		157 ksi
@Temperature 73.4 °F		DAM; ISO 527
Izod Impact, Notched (ISO)  13.0 kJ/m²
@Temperature -30.0 °C		6.19 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 13.0 kJ/m²
@Temperature -30.0 °C		6.19 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 27.0 kJ/m²
@Temperature 23.0 °C		12.8 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 66.0 kJ/m²
@Temperature 23.0 °C		31.4 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Charpy Impact, Notched  1.50 J/cm²
@Temperature -30.0 °C		7.14 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 1.50 J/cm²
@Temperature -30.0 °C		7.14 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 4.00 J/cm²
@Temperature 23.0 °C		19.0 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 8.00 J/cm²
@Temperature 23.0 °C		38.1 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C185 °FDAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 46.0 °C115 °FDAM; ISO 75-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 218 °C424 °F10°C/min; DAM; ISO 11357-1/-3
 240 °C464 °FDAM; Optimum; Extrusion
 230 - 250 °C446 - 482 °FDAM; Extrusion
 250 °C482 °FDAM; Optimum; Injection Molding
 230 - 290 °C446 - 554 °FDAM; Injection Molding
Mold Temperature 70.0 °C158 °FDAM; optimum; Injection Molding
 50.0 - 90.0 °C122 - 194 °FDAM; Injection Molding
Drying Temperature 80.0 °C176 °FDAM; Injection Molding
 80.0 °C176 °FDAM; Extrusion
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM; Injection Molding
 3.00 - 4.00 hour3.00 - 4.00 hourDAM; Extrusion
Moisture Content <= 0.050 %<= 0.050 %DAM; Extrusion
 <= 0.050 %<= 0.050 %DAM; Injection Molding
 
Descriptive Properties
AppearanceBlack ColorDAM
FeaturesFlexibility, GoodDAM
 Flexibility, GoodDAM
 Toughness, GoodDAM
 Toughness, GoodDAM
FormsPelletsDAM
GenericNylon 612DAM
Material StatusPreliminary DataDAM
Part Marking Code>PA612-HI<ISO 11469; DAM
Processing MethodExtrusionDAM
Product CategoryExtrusion ResinsDAM
 Toughened ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA612-HIISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47509.html

免责声明: 本文 DuPont Performance Polymers Zytel® LC6200 BK385 Nylon 612 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4