PolyOne Edgetek® NL-20CF/000 Nylon 6/12, Carbon Fiber Reinforced

PolyOne Edgetek® NL-20CF/000 Nylon 6/12, Carbon Fiber Reinforced 物性表: PolyOne Edgetek® NL-20CF/000 Nylon 6/12, Carbon Fiber Reinforced物性表及特性介绍,PolyOne Edgetek® NL-20CF/000 Nylon 6/12, Carbon Fiber Reinforced注塑参数详情,如需PolyOne Edgetek® NL-20CF/000 Nylon 6/12, Carbon Fiber Reinforced下载, 可到相关下载区下载
  • 吸水率 [%]: 0.24
  • 缺口冲击强度: 1.07
  • 弯曲强度 [MPa]: 179.0
  • 弯曲模量 [MPa]: 11.7
  • 热变形温度 [℃]: 216.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.15 g/cc1.15 g/ccASTM D792
Water Absorption 0.24 %
@Thickness 3.17 mm
0.24 %
@Thickness 0.125 in
24 hr. Immersion; ASTM D570
Water Absorption at Saturation 2.2 %
@Thickness 3.17 mm
2.2 %
@Thickness 0.125 in
Long-Term Immersion; ASTM D570
Linear Mold Shrinkage 0.0020 - 0.0030 cm/cm0.0020 - 0.0030 in/inASTM D955
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Ultimate 179 MPa26000 psiType 1 - Rigids, 0.2 in/min; ASTM D638
Elongation at Break 4.0 %4.0 %Type 1 - Rigids, 0.2 in/min; ASTM D638
Flexural Strength 276 MPa40000 psiASTM D790
Flexural Modulus 11.7 GPa1700 ksiASTM D790
Compressive Strength 145 MPa21000 psiASTM D695
Izod Impact, Notched 1.07 J/cm
@Thickness 6.35 mm,
Temperature 23.0 °C
2.00 ft-lb/in
@Thickness 0.250 in,
Temperature 73.4 °F
Method A, Injection Molded; ASTM D256
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 10000 ohm-cm10000 ohm-cmASTM D257
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 216 °C420 °FUnannealed, 0.125 in bars; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 213 °C415 °FUnannealed, 0.125 in bars; ASTM D648

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47523.html

免责声明: 本文 PolyOne Edgetek® NL-20CF/000 Nylon 6/12, Carbon Fiber Reinforced 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4