- 吸水率 [%]: 0.15
- 缺口冲击强度: 0.96
- 拉伸强度 [MPa]: 119.0
- 弯曲模量 [MPa]: 7.24
- 热变形温度 [℃]: 212.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 | ||
| Water Absorption | 0.15 % | 0.15 % | @ 24 hrs; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 119 MPa | 17300 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 119 MPa | 17300 psi | ASTM D638 | ||
| Elongation at Break | 3.6 % | 3.6 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 8.45 GPa | 1230 ksi | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 191 MPa | 27700 psi | ASTM D790 | ||
| Flexural Modulus | 7.24 GPa | 1050 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.960 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 1.80 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Coefficient of Friction, Dynamic | 0.13 | 0.13 | vs. Steel - Dynamic; ASTM D1894 | ||
| Coefficient of Friction, Static | 0.18 | 0.18 | vs. Steel - Static; ASTM D1894 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C | 10.0 µin/in-°F | ISO 11359-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C @Thickness 3.18 mm | 414 °F @Thickness 0.125 in | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C @Thickness 3.18 mm | 383 °F @Thickness 0.125 in | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 243 - 271 °C | 469 - 520 °F | |||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| Drying Temperature | 71.1 - 76.7 °C | 160 - 170 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Descriptive Properties | |||||
| Appearance | Black | ||||
| Features | Good Wear Resistance | ||||
| High Stiffness | |||||
| Lubricated | |||||
| Forms | Pellets | ||||
| Generic Material | Nylon 612 | ||||
| Generic Name | Polyamide 612 (Nylon 612) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| RoHS Compliance | RoHS Compliant | ||||
| Uses | Appliance Components | ||||
| Automotive Applications | |||||
| Bearings | |||||
| Business Equipment | |||||
| Consumer Applications | |||||
| Conveyor Parts | |||||
| Gears | |||||
| Industrial Applications | |||||
| Printer Parts | |||||
| Pulleys | |||||
| Rollers | |||||