- 密度 [g/cm3]: 1.24
- 吸水率 [%]: 0.15
- 缺口冲击强度: 0.69
- 断裂伸长率 [%]: 117
- 弯曲强度 [MPa]: 69.0
- 弯曲模量 [MPa]: 3.40
- 热变形温度 [℃]: 199.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0090 - 0.010 cm/cm @Thickness 3.17 mm | 0.0090 - 0.010 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 69.0 MPa | 10000 psi | ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | ASTM D638 |
| Tensile Modulus | 3.40 GPa | 493 ksi | ASTM D638 |
| Flexural Yield Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 3.40 GPa | 493 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 - 0.960 J/cm @Thickness 6.35 mm | 1.29 - 1.80 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 199 °C | 390 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C | 379 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 238 - 271 °C | 460 - 520 °F | Stock |
| Mold Temperature | 93.0 - 107 °C | 199 - 225 °F | |
| Drying Temperature | 93.0 - 107 °C | 199 - 225 °F | |