- 密度 [g/cm3]: 1.06
- 拉伸强度 [MPa]: 52.0
- 热变形温度 [℃]: 170.0
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 | ||
Mechanical Properties | Metric | English | Comments | ||
Tensile Strength, Yield | 52.0 MPa | 7540 psi | ISO 527-2/1A | ||
Elongation at Break | >= 50 % | >= 50 % | ISO 527-2/1A | ||
Elongation at Yield | 20 % | 20 % | ISO 527-2/1A | ||
Tensile Modulus | 1.70 GPa | 247 ksi | ISO 527-2/1A | ||
Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | ||
NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
0.900 J/cm² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
Thermal Properties | Metric | English | Comments | ||
Melting Point | 215 °C | 419 °F | Peak Temperature; ISO 3146, ISO 11357 | ||
Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | When conditioned at 180°C for 1 hour; ISO 75 | ||
Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75 | ||
75.0 °C | 167 °F | When conditioned at 180°C for 1 hour; ISO 75 | |||
Vicat Softening Point | 180 °C | 356 °F | 50N; ISO 306 | ||
Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||||
Descriptive Properties | |||||
Electrolytic Corrosion | A1 Step | IEC 60426 |