- 密度 [g/cm3]: 1.02
- 吸水率 [%]: 2.2
- 拉伸强度 [MPa]: 30.0
- 热变形温度 [℃]: 140.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.50 % | 0.50 % | 23°C/50% R.H.; ISO 62 |
| Water Absorption at Saturation | 2.2 % | 2.2 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ISO 527-2/1A |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-2/1A |
| Elongation at Yield | 12 % | 12 % | ISO 527-2/1A |
| Tensile Modulus | 1.05 GPa | 152 ksi | ISO 527-2/1A |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 1.90 J/cm² @Temperature -30.0 °C | 9.04 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 9.00 J/cm² @Temperature 23.0 °C | 42.8 ft-lb/in² @Temperature 73.4 °F | Partial Break; ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 170 µm/m-°C @Temperature 23.0 - 55.0 °C | 94.4 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75 |
| Vicat Softening Point | 110 °C | 230 °F | 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||