- 熔体流动速率 [g/10min]: 42.8
- 密度 [g/cm3]: 1.07
- 吸水率 [%]: 2.8
- 拉伸强度 [MPa]: 60.0
- 弯曲模量 [MPa]: 2.50
- 热变形温度 [℃]: 155.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 2.8 % | 2.8 % | ISO 62 |
| Melt Flow | 42.8 g/10 min @Load 5.00 kg, Temperature 275 °C | 42.8 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/2 |
| Elongation at Break | >= 30 % | >= 30 % | ISO 527-1/2 |
| Elongation at Yield | 10 % | 10 % | ISO 527-1/2 |
| Tensile Modulus | 2.10 GPa | 305 ksi | ISO 527-1/-2 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 0.800 J/cm² @Temperature 23.0 °C | 3.81 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 7.00e+13 ohm-cm | 7.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 5.00e+12 ohm | 5.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.9 @Frequency 1e+6 Hz | 3.9 @Frequency 1e+6 Hz | IEC 60250 |
| 4.4 @Frequency 100 Hz | 4.4 @Frequency 100 Hz | IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | K20/P50; IEC 60243-1 |
| Dissipation Factor | 0.039 @Frequency 1e+6 Hz | 0.039 @Frequency 1e+6 Hz | IEC 60250 |
| 0.059 @Frequency 100 Hz | 0.059 @Frequency 100 Hz | IEC 60250 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75-1/-2 |
| Vicat Softening Point | 185 °C | 365 °F | Method B, 50 N; ISO 306 |
| 210 °C | 410 °F | Method A, 10 N; ISO 306 | |
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | IEC 60695 |
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695 | |