- 密度 [g/cm3]: 1.31
- 缺口冲击强度: 1.38
- 弯曲模量 [MPa]: 8.83
- 热变形温度 [℃]: 213.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| 1.322 g/cc | 0.04776 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.170 % | 0.170 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0011 - 0.0016 cm/cm @Time 86400 sec | 0.0011 - 0.0016 in/in @Time 24.0 hour | ISO 294 |
| 0.0010 - 0.0020 cm/cm @Time 86400 sec | 0.0010 - 0.0020 in/in @Time 24.0 hour | ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0066 - 0.0071 cm/cm @Time 86400 sec | 0.0066 - 0.0071 in/in @Time 24.0 hour | ISO 294 |
| 0.0070 - 0.0080 cm/cm @Time 86400 sec | 0.0070 - 0.0080 in/in @Time 24.0 hour | ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 178 MPa | 25800 psi | ISO 527 |
| 182 MPa | 26400 psi | ASTM D638 | |
| Elongation at Break | 3.4 % | 3.4 % | ISO 527 |
| 3.7 % | 3.7 % | ASTM D638 | |
| Tensile Modulus | 9.58 GPa | 1390 ksi | 50 mm/min; ASTM D638 |
| 10.32 GPa | 1497 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 |
| 291 MPa | 42200 psi | ASTM D790 | |
| Flexural Modulus | 8.83 GPa | 1280 ksi | ISO 178 |
| 9.30 GPa | 1350 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.38 J/cm | 2.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 12.38 J/cm | 23.19 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 78.0 kJ/m² | 37.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 14.0 J | 10.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 40.5 µm/m-°C @Temperature -40.0 - 40.0 °C | 22.5 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 40.5 µm/m-°C @Temperature -40.0 - 40.0 °C | 22.5 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 73.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 40.6 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 73.1 µm/m-°C @Temperature -40.0 - 40.0 °C | 40.6 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C @Thickness 3.20 mm | 415 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C @Thickness 3.20 mm | 388 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL 94 by SABIC-IP |