- 密度 [g/cm3]: 1.31
- 缺口冲击强度: 0.85
- 弯曲模量 [MPa]: 7.79
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 135 MPa | 19600 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 8.75 GPa | 1270 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| Flexural Modulus | 7.79 GPa | 1130 ksi | ASTM D790 |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.87 J/cm | 11.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C @Thickness 3.20 mm | 388 °F @Thickness 0.126 in | unannealed; ASTM D648 |