- 密度 [g/cm3]: 1.33
- 缺口冲击强度: 0.96
- 弯曲模量 [MPa]: 9.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 173 MPa | 25100 psi | ASTM D638 |
| Elongation at Break | 3.2 % | 3.2 % | ASTM D638 |
| Tensile Modulus | 9.37 GPa | 1360 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
| Flexural Modulus | 9.10 GPa | 1320 ksi | ASTM D790 |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.51 J/cm | 19.69 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C @Thickness 3.20 mm | 406 °F @Thickness 0.126 in | unannealed; ASTM D648 |