- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 0.85
- 弯曲模量 [MPa]: 16.68
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D 792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 174 MPa | 25200 psi | ASTM D 638 |
| Elongation at Break | 1.7 % | 1.7 % | ASTM D 638 |
| Tensile Modulus | 19.92 GPa | 2889 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 275 MPa | 39900 psi | ASTM D 790 |
| Flexural Modulus | 16.68 GPa | 2419 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.850 J/cm @Temperature 23.0 °C | 1.59 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 8.01 J/cm @Temperature 23.0 °C | 15.0 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C @Thickness 3.20 mm | 390 °F @Thickness 0.126 in | unannealed; ASTM D 648 |