- 密度 [g/cm3]: 1.28
- 吸水率 [%]: 0.25
- 缺口冲击强度: 9.0
- 拉伸强度 [MPa]: 120.0
- 断裂伸长率 [%]: 185
- 弯曲模量 [MPa]: 6.05
- 热变形温度 [℃]: 209.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| Water Absorption | 0.25 % @Time 86400 sec | 0.25 % @Time 24.0 hour | ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 120 MPa | 17400 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.1 % | 2.1 % | 5 mm/min; ISO 527 |
| 4.2 % | 4.2 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Tensile Modulus | 7.80 GPa | 1130 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 185 MPa | 26800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.05 GPa | 877 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 39.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 21.7 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 160 µm/m-°C @Temperature 23.0 - 60.0 °C | 88.9 µin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 209 °C | 408 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 188 °C | 370 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |