- 密度 [g/cm3]: 1.41
- 缺口冲击强度: 1.58
- 断裂伸长率 [%]: 233
- 弯曲模量 [MPa]: 9.70
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.160 % | 0.160 % | 50% RH, 24 hrs; ASTM D570 |
| 0.280 % | 0.280 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec | 0.0010 - 0.0030 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec | 0.010 - 0.030 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 156 MPa | 22600 psi | Type I, 5 mm/min; ASTM D638 |
| 157 MPa | 22800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.8 % | 2.8 % | 5 mm/min; ISO 527 |
| 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 11.81 GPa | 1713 ksi | 1 mm/min; ISO 527 |
| 12.12 GPa | 1758 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 233 MPa | 33800 psi | ISO 178 |
| 235 MPa | 34100 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 233 MPa | 33800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 9.70 GPa | 1410 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.98 GPa | 1450 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.58 J/cm | 2.96 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.95 J/cm | 18.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 62.0 kJ/m² | 29.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 20.0 J @Temperature 23.0 °C | 14.8 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 39.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 21.7 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 41.7 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 214 °C @Thickness 3.20 mm | 417 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C | 385 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 198 °C @Thickness 3.20 mm | 388 °F @Thickness 0.126 in | unannealed; ASTM D648 | |