- 密度 [g/cm3]: 1.35
- 缺口冲击强度: 0.96
- 拉伸强度 [MPa]: 115.0
- 弯曲模量 [MPa]: 5.51
- 热变形温度 [℃]: 212.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec | 0.0030 - 0.0050 in/in @Time 24.0 hour | ASTM D955 |
| 0.0041 cm/cm @Time 86400 sec | 0.0041 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.012 cm/cm @Time 86400 sec | 0.010 - 0.012 in/in @Time 24.0 hour | ASTM D955 |
| 0.011 cm/cm @Time 86400 sec | 0.011 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 115 MPa | 16700 psi | ASTM D638 |
| 121 MPa | 17500 psi | ISO 527 | |
| Tensile Strength, Yield | 115 MPa | 16700 psi | ASTM D638 |
| 121 MPa | 17500 psi | ISO 527 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| 3.1 % | 3.1 % | ASTM D638 | |
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527 |
| 3.1 % | 3.1 % | ASTM D638 | |
| Tensile Modulus | 6.89 GPa | 999 ksi | 50 mm/min; ASTM D638 |
| 7.10 GPa | 1030 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 172 MPa | 24900 psi | ASTM D790 |
| 176 MPa | 25500 psi | ISO 178 | |
| Flexural Modulus | 5.51 GPa | 799 ksi | ASTM D790 |
| 6.10 GPa | 885 ksi | ISO 178 | |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.29 J/cm | 17.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 53.0 kJ/m² | 25.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.46 | 0.46 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.47 | 0.47 | ASTM D3702 Modified |
| K (wear) Factor | 36.3 x 10-8 mm³/N-M | 18.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 99.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 55.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 99.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 55.0 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 39.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 21.7 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 39.6 µm/m-°C @Temperature -40.0 - 40.0 °C | 22.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 212 °C @Thickness 3.20 mm | 414 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 197 °C @Thickness 3.20 mm | 387 °F @Thickness 0.126 in | unannealed; ASTM D648 | |