TP Composites HiFill® PA6/12 CF30 BK 30% Carbon Filled

TP Composites HiFill® PA6/12 CF30 BK 30% Carbon Filled 物性表: TP Composites HiFill® PA6/12 CF30 BK 30% Carbon Filled物性表及特性介绍,TP Composites HiFill® PA6/12 CF30 BK 30% Carbon Filled注塑参数详情,如需TP Composites HiFill® PA6/12 CF30 BK 30% Carbon Filled下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.22
  • 吸水率 [%]: 0.16
  • 缺口冲击强度: 1.07
  • 拉伸强度 [MPa]: 200.0
  • 弯曲模量 [MPa]: 15.9
  • 硬度: 118.0
  • 热变形温度 [℃]: 221.0
 
Physical PropertiesMetricEnglishComments
Density 1.22 g/cc0.0441 lb/in³ASTM D792
Water Absorption 0.16 %
@Time 86400 sec
0.16 %
@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0030 cm/cm
@Thickness 3.17 mm
0.0030 in/in
@Thickness 0.125 in
ASTM D955
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell R 118118ASTM D785
Tensile Strength, Yield 200 MPa29000 psiASTM D638
Elongation at Break 2.2 %2.2 %ASTM D638
Flexural Strength 303 MPa44000 psiASTM D790
Flexural Modulus 15.9 GPa2300 ksiASTM D790
Izod Impact, Notched 1.07 J/cm
@Thickness 3.17 mm
2.00 ft-lb/in
@Thickness 0.125 in
ASTM D256
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 19.8 µm/m-°C11.0 µin/in-°FASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 221 °C430 °FUnannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 216 °C420 °FUnannealed; ASTM D648

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-47815.html

免责声明: 本文 TP Composites HiFill® PA6/12 CF30 BK 30% Carbon Filled 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4