- 密度 [g/cm3]: 1.03
- 缺口冲击强度: 65.0
- 拉伸强度 [MPa]: 32.0
- 热变形温度 [℃]: 110.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.015 cm/cm @Thickness 2.00 mm | 0.015 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm @Thickness 2.00 mm | 0.012 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 32.0 MPa @Temperature 23.0 °C | 4640 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 40.0 MPa @Temperature 23.0 °C | 5800 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 35 % @Temperature 23.0 °C | 35 % @Temperature 73.4 °F | 50mm/min; DAM; ISO 527 | ||
| 65 % @Temperature 23.0 °C | 65 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | |||
| 200 % @Temperature 23.0 °C | 200 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| 250 % @Temperature 23.0 °C | 250 % @Temperature 73.4 °F | 50mm/min; 50%RH; ISO 527 | |||
| Elongation at Yield | 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 30 % @Temperature 23.0 °C | 30 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 0.800 GPa @Temperature 23.0 °C | 116 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 1.50 GPa @Temperature 23.0 °C | 218 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Izod Impact, Notched (ISO) | 65.0 kJ/m² @Temperature 23.0 °C | 30.9 ft-lb/in² @Temperature 73.4 °F | partial break; DAM; ISO 180/1A | ||
| 80.0 kJ/m² @Temperature 23.0 °C | 38.1 ft-lb/in² @Temperature 73.4 °F | partial break; 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 7.00 J/cm² @Temperature 23.0 °C | 33.3 ft-lb/in² @Temperature 73.4 °F | partial break; DAM; ISO 179/1eA | ||
| 9.50 J/cm² @Temperature 23.0 °C | 45.2 ft-lb/in² @Temperature 73.4 °F | partial break; 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 223 °C | 433 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 260 °C | 500 °F | DAM; Optimum; Injection Molding | |||
| 250 - 270 °C | 482 - 518 °F | DAM; Injection Molding | |||
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | DAM; Injection Molding | ||
| 70.0 °C | 158 °F | DAM; optimum; Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Injection Molding | ||
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | DAM; Injection Molding | ||
| Moisture Content | <= 0.10 % | <= 0.10 % | DAM; Injection Molding | ||
| Descriptive Properties | |||||
| Features | Renewable Resource Content | ||||
| Forms | Pellets | DAM | |||
| Generic | PA610-I | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Part Marking Code | >PA610-I< | ISO 11469; DAM | |||
| Processing Method | injection Molding | DAM | |||
| Product Category | Renewably Sourced Resins | DAM | |||
| Toughened Resins | DAM | ||||
| Unreinforced Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA610-I | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||