- 熔体流动速率 [g/10min]: 39.3
- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 2.0
- 弯曲模量 [MPa]: 7.90
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 | ||
| Water Absorption | 2.0 - 2.6 % | 2.0 - 2.6 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.80 - 1.2 % | 0.80 - 1.2 % | ISO 62 | ||
| Viscosity Measurement | 150 | 150 | [cm3/g]; ISO 307 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | Test Box 1.5 mm | ||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ISO 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 2577 | ||
| Melt Flow | 39.3 g/10 min @Load 5.00 kg, Temperature 275 °C | 39.3 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527-1/-2 | ||
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1/-2 | ||
| Modulus of Elasticity | 8.40 GPa | 1220 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 230 MPa | 33400 psi | ISO 178 | ||
| Flexural Modulus | 7.90 GPa | 1150 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature -30.0 °C | 40.4 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 9.00 J/cm² @Temperature 23.0 °C | 42.8 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -30.0 °C | 3.81 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.30 J/cm² @Temperature 23.0 °C | 6.19 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ISO 11357-1/-3 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection molding | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection molding/Extrusion | ||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||