- 密度 [g/cm3]: 1.04
- 弯曲模量 [MPa]: 0.690
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183/A | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 40.0 MPa | 5800 psi | ISO 527 Type 1A | ||
| Elongation at Break | 150 % | 150 % | ISO 527 Type 1A | ||
| Tensile Modulus | 0.800 GPa | 116 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 30.0 MPa | 4350 psi | ISO 178 | ||
| Flexural Modulus | 0.690 GPa | 100 ksi | ISO 178 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C | 7.14 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 8.70 J/cm² @Temperature 23.0 °C | 41.4 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ISO 1210 | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ISO 1210 | |||
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ISO 1210 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 215 - 225 °C | 419 - 437 °F | |||
| Front Barrel Temperature | 225 - 235 °C | 437 - 455 °F | |||
| Die Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Melt Temperature | 215 °C | 419 °F | ISO 11357 | ||
| Moisture Content | <= 0.10 % | <= 0.10 % | |||
| Descriptive Properties | |||||
| Compression Zone | 225-235°C | ||||