- 密度 [g/cm3]: 1.28
- 缺口冲击强度: 1.27
- 拉伸强度 [MPa]: 233.0
- 断裂伸长率 [%]: 362
- 弯曲模量 [MPa]: 20.27
- 热变形温度 [℃]: 223.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.310 % | 0.310 % | 50% RH, 24 hrs; ASTM D570 |
| 0.310 % | 0.310 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.00060 - 0.00080 cm/cm @Time 86400 sec | 0.00060 - 0.00080 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0070 cm/cm @Time 86400 sec | 0.0060 - 0.0070 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 233 MPa | 33800 psi | Type I, 5 mm/min; ASTM D638 |
| 237 MPa | 34400 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 233 MPa | 33800 psi | Type I, 5 mm/min; ASTM D638 |
| 237 MPa | 34400 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 31.86 GPa | 4621 ksi | 1 mm/min; ISO 527 |
| 44.2 GPa | 6410 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 362 MPa | 52500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 20.27 GPa | 2940 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 22.44 GPa | 3255 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.27 J/cm | 2.38 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.44 J/cm | 25.18 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 68.0 kJ/m² | 32.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 7.94 µm/m-°C @Temperature -40.0 - 40.0 °C | 4.41 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| CTE, linear, Transverse to Flow | 8.27 µm/m-°C @Temperature -40.0 - 40.0 °C | 4.59 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 222 °C @Thickness 3.20 mm | 432 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 421 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 217 °C @Thickness 3.20 mm | 423 °F @Thickness 0.126 in | unannealed; ASTM D648 | |