- 密度 [g/cm3]: 1.14
- 缺口冲击强度: 0.39
- 弯曲模量 [MPa]: 2.04
- 热变形温度 [℃]: 143.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.260 % | 0.260 % | 50% RH, 24 hrs; ASTM D570 |
| 0.380 % | 0.380 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.030 cm/cm @Time 86400 sec | 0.0090 - 0.030 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.040 cm/cm @Time 86400 sec | 0.010 - 0.040 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 5 mm/min; ASTM D638 |
| 61.0 MPa | 8850 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 |
| 4.5 % | 4.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.48 GPa | 360 ksi | 1 mm/min; ISO 527 |
| 2.68 GPa | 389 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 73.0 MPa | 10600 psi | ISO 178 |
| Flexural Modulus | 2.04 GPa | 296 ksi | 2 mm/min; ISO 178 |
| 2.27 GPa | 329 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.390 J/cm | 0.731 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.99 J/cm | 7.47 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 42.0 kJ/m² | 20.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J @Temperature 23.0 °C | 2.21 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.38 | 0.38 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.25 | 0.25 | ASTM D3702 Modified |
| K (wear) Factor | 70.5 x 10-8 mm³/N-M | 35.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 112 µm/m-°C @Temperature -30.0 - 30.0 °C | 62.2 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 115 µm/m-°C @Temperature -30.0 - 30.0 °C | 63.9 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 164 °C @Thickness 3.20 mm | 327 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 63.0 °C @Thickness 3.20 mm | 145 °F @Thickness 0.126 in | unannealed; ASTM D648 | |