- 密度 [g/cm3]: 1.24
- 缺口冲击强度: 0.48
- 弯曲模量 [MPa]: 5.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 111 MPa | 16100 psi | ASTM D638 |
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638 |
| Tensile Modulus | 6.37 GPa | 924 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 158 MPa | 22900 psi | ASTM D790 |
| Flexural Modulus | 5.92 GPa | 859 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.32 J/cm | 8.09 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C @Thickness 3.20 mm | 397 °F @Thickness 0.126 in | unannealed; ASTM D648 |