Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 0.980 g/cc | 0.980 g/cc | ISO 2782 | ||
Viscosity Measurement | 16 @Temperature 150 °C | 16 @Temperature 302 °F | Kg/cm2; Macklow-Smith extrusion rheometer | ||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore A | 80 | 80 | ISO 868 | ||
Tensile Strength | 17.8 MPa | 2580 psi | ISO 37 | ||
Elongation at Break | 765 % | 765 % | ISO 37 | ||
100% Modulus | 0.00380 GPa | 0.551 ksi | ISO 37 | ||
200% Modulus | 0.00440 GPa | 0.638 ksi | ISO 37 | ||
300% Modulus | 0.00530 GPa | 0.769 ksi | ISO 37 | ||
Tear Strength | 61.0 kN/m | 348 pli | ISO 34-B | ||
Abrasion | 94 | 94 | mm3; DIN 53516 | ||
Compression Set | 36 % @Temperature 22.0 °C, Time 259000 sec | 36 % @Temperature 71.6 °F, Time 72.0 hour | ISO 815 | ||
46 % @Temperature 70.0 °C, Time 79200 sec | 46 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
62 % @Temperature 100 °C, Time 79200 sec | 62 % @Temperature 212 °F, Time 22.0 hour | ISO 815 | |||
Thermal Properties | Metric | English | Comments | ||
Maximum Service Temperature, Air | 125 °C | 257 °F | |||
Minimum Service Temperature, Air | -60.0 °C | -76.0 °F | |||
Descriptive Properties | |||||
Bonds with | Polypropylene | ||||
Chemical Resistance | Acetone | Moderate/Good | |||
Acids up to 80% | Excellent | ||||
Alcohol | Excellent | ||||
Alkalis | Excellent | ||||
Brake fluid | Good | ||||
Chlorinate solvents | Poor | ||||
Diesel | Poor | ||||
Ethylene glycol | Excellent | ||||
Gasoline | Poor | ||||
Salt solution | Excellent | ||||
Soda lye | Excellent | ||||
Water, 23°C | Excellent | ||||
Water, 95°C | Good |